The invention relates to a composition for intuitively inspecting welding strength and a preparation method thereof, which comprises the following components by weight: 100 parts of polymer, 1-3 parts of thermal assistant, 0.1-2 parts of inorganic developer and 0-2 parts of organic color powder. By adding thermistor and inorganic color developing agent, the material is welded at a certain welding temperature, the color of the weld will change, and the color will be saved at normal temperature after discoloration, so as to visually inspect whether the temperature of the weld reaches the required welding temperature, and before that, it is found that the welding is not firm or cracked due to insufficient temperature.
【技术实现步骤摘要】
一种用于直观检验焊接强度的组合物及其制备方法
本专利技术属于塑胶热焊接强度检测
,特别涉及一种用于直观检验焊接强度的组合物及其制备方法。
技术介绍
为了在使用过程中防止漏液或者渗水,许多塑料产品需要进行热焊接密封处理,例如蓄电池和水泵外壳。热焊接技术需要配合适当的塑胶材料、焊接设备、焊接工艺和焊接温度才能得到较好的焊接强度以达到较优的密封效果,然而经常会由于焊接设备的老化,焊接温度不稳定导致产品热焊接效果不好,在焊接缝处产生开裂。有时候这种焊缝开裂不是在焊接的时候马上就能发现的,会过一段时间,做成成品后才出现开裂,这种在后端使用后才出现的开裂有可能会导致更大的安全风险和更多的经济损失。
技术实现思路
本专利技术所要解决的技术问题是提供一种用于直观检验焊接强度的组合物及其制备方法,该组合物在一定的焊接温度下焊接,焊缝处颜色会发生变化,变色后的颜色在常温会保存下来,从而可视化的检验焊缝处温度是否达到所需要的焊接温度,提前发现由于温度不够导致焊接不牢或开裂的问题。本专利技术提供了一种用于直观检验焊接强度的组合物,按重量份数,包括以下组分:聚合物100份,热敏助剂1~3份,无机显色剂0.1~2份,有机色粉0~2份。所述聚合物为乙烯基类聚合物、苯基类聚合物、聚酯类聚合物中的一种或几种。所述热敏助剂为吡咯并吡咯二酮类化合物。由于吡咯并吡咯二酮类化合物分子的发色体系和苯环之间产生强烈的共轭作用,单个分子的状态与堆积态会呈现不一样的颜色,因此可以通过调控吡咯并吡咯二酮类化合物 ...
【技术保护点】
1.一种用于直观检验焊接强度的组合物,其特征在于:按重量份数,包括以下组分:/n聚合物100份,热敏助剂1~3份,无机显色剂0.1~2份,有机色粉0~2份。/n
【技术特征摘要】
1.一种用于直观检验焊接强度的组合物,其特征在于:按重量份数,包括以下组分:
聚合物100份,热敏助剂1~3份,无机显色剂0.1~2份,有机色粉0~2份。
2.根据权利要求1所述的组合物,其特征在于:所述聚合物为乙烯基类聚合物、苯基类聚合物、聚酯类聚合物中的一种或几种。
3.根据权利要求1所述的组合物,其特征在于:所述热敏助剂为吡咯并吡咯二酮类化合物。
4.根据权利要求1所述的组合物,其特征在于:所述无机显色剂为水滑石、氮化硼、滑石粉中的一种或几种。
5.根据权利要...
【专利技术属性】
技术研发人员:刘乐文,黄池光,范聪成,李斌,杜荣华,付锦峰,杨霄云,夏建盟,
申请(专利权)人:江苏金发科技新材料有限公司,上海金发科技发展有限公司,
类型:发明