耐高温水性漆制造技术

本发明专利技术提出了一种耐高温水性漆，按照重量份数计算，包括以下组分：环氧改性有机硅树脂40～50份、水性氨基树脂15～25份、交联树脂4～8份、改性镁铝水滑石8～16份、纳米碳酸钙3～6份、助剂4～10份及水40～60份；所述改性镁铝水滑石主要由镁铝水滑石、氮化硅与硅烷偶联剂制备得到。该耐高温水性漆能够耐受至少800℃高温，附着力与防腐性能优异。

High temperature resistant waterborne paint

The invention provides a high temperature resistant water-based paint, which comprises the following components according to the weight parts: 40-50 parts of epoxy modified silicone resin, 15-25 parts of water-based amino resin, 4-8 parts of cross-linked resin, 8-16 parts of modified magnesium aluminum hydrotalcite, 3-6 parts of nano calcium carbonate, 4-10 parts of auxiliary agent and 40-60 parts of water; the modified magnesium aluminum hydrotalcite is mainly composed of magnesium aluminum hydrotalcite, silicon nitride and silicon Alkane coupling agent was prepared. The high temperature resistant water-based paint can withstand at least 800 \u2103, and has excellent adhesion and corrosion resistance.

【技术实现步骤摘要】
耐高温水性漆
本专利技术属于油漆
，具体涉及一种耐高温水性漆。
技术介绍
随着人类生活质量的提高，环保法规也越来越严格，各种环保条例对挥发性有机化合物(VOC)的排放量、有害溶剂及各种重金属的含量都有严格限制。20世纪90年代，在全世界范围内掀起了减少涂料中溶剂含量和VOC的行动，该行动对工业涂料及特种涂料行业产生了较大影响。因此，发展绿色环保型涂料已成为涂料行业发展的趋势。凡是用水作溶剂或者作分散介质的涂料，都可称为水性漆。水性漆具有诸多优点，例如以水作溶剂，可节省大量资源；水性涂料消除了施工时火灾危险性；降低了对大气污染；在湿表面和潮湿环境中可以直接涂覆施工；水性涂料对材质表面适应性好，涂层附着力强；水性涂料涂装工具可用水清洗，大大减少清洗溶剂的消耗等等。因此，在耐高温领域使用水性漆也是一个趋势。例如CN101619197A公开了一种纳米水性耐高温金属烘烤涂料，所述纳米水性耐高温金属烘烤涂料由A、B组分配合组成，其各自的配方组成如下(按重量计％)：A组分：水性耐高温纳米树脂80-90，水性铝银浆或珠光颜料4-10，分散本文档来自技高网...

【技术保护点】
1.一种耐高温水性漆，其特征在于，按照重量份数计算，包括以下组分：/n环氧改性有机硅树脂40～50份、水性氨基树脂15～25份、交联树脂4～8份、改性镁铝水滑石8～16份、纳米碳酸钙3～6份、助剂4～10份及水40～60份；所述改性镁铝水滑石主要由镁铝水滑石、氮化硅与硅烷偶联剂制备得到。/n

【技术特征摘要】
1.一种耐高温水性漆，其特征在于，按照重量份数计算，包括以下组分：
环氧改性有机硅树脂40～50份、水性氨基树脂15～25份、交联树脂4～8份、改性镁铝水滑石8～16份、纳米碳酸钙3～6份、助剂4～10份及水40～60份；所述改性镁铝水滑石主要由镁铝水滑石、氮化硅与硅烷偶联剂制备得到。


2.根据权利要求1所述的耐高温水性漆，其特征在于，所述改性镁铝水滑石的制备方法包括以下步骤：
将镁铝水滑石与氮化硅加入到二甲苯中，进行超声分散，得到分散液，将分散液升温至70～90℃，然后依次加入硅烷偶联剂与水，搅拌均匀反应4～8h...

【专利技术属性】
技术研发人员：汪琦，郭元，
申请(专利权)人：芜湖市棠华建材科技有限公司，
类型：发明
国别省市：安徽;34