The invention discloses a red mud treatment method, which relates to the technical field of harmless treatment of industrial waste. The method includes: washing the red mud with washing water to obtain diluent, stirring with air at the bottom of the tank, washing operation lasting for 2 \u2011 3 hours; introducing diluent into centrifuge for solid-liquid separation operation to obtain the filtrate with main component of iron metal compound; and The filtrate is well mixed with iron oxide catalyst, charcoal mud, glucose and baking soda, and fully combusted by self ignition under the condition of 500 \u2011 800 \u2103 oxygen enrichment. After 5 \u2011 6 hours, the filtrate is sintered into a block with porous structure to obtain the solidified iron oxide. Through the red mud treatment method of the invention, the resource-based and harmless red mud treatment is realized.
【技术实现步骤摘要】
一种红泥的处理方法
本专利技术涉及工业废料的无害化处理
，具体涉及一种红泥的处理方法。
技术介绍
在工业冶金制造过程中，将产生大量“红泥”，且其粘度较大，由于其含铁元素致色属性使得其滴落到任何地方都是红红的一片，极难清理，且其危害性若将其随意排放将对环境影响很大。目前，红泥普遍采取简单的外运堆填方法进行处理，存在二次污染环境的隐患，而且其中的铁元素无法有效利用，造成资源浪费。
技术实现思路
因此，本专利技术实施例目的在于提供一种无害化、资源化的红泥的处理方法。为此，本专利技术实施例的一种红泥的处理方法，包括以下步骤：S1、用洗涤水对红泥进行洗涤获得稀释液，同时在池底鼓风进行搅拌，洗涤操作持续2-3小时；S2、将稀释液通入离心机进行固液分离操作，获得主要成分为铁金属化合物的滤出物；S3、将滤出物与铁氧化催化剂、木炭泥、葡萄糖、小苏打混合均匀，在500-800℃的富氧条件下通过自燃充分燃烧，进行5-6小时后，烧结成具有多孔隙结构的块状体，获得三氧化二铁固化物。
【技术保护点】
1.一种红泥的处理方法，其特征在于，包括以下步骤：/nS1、用洗涤水对红泥进行洗涤获得稀释液，同时在池底鼓风进行搅拌，洗涤操作持续2-3小时；/nS2、将稀释液通入离心机进行固液分离操作，获得主要成分为铁金属化合物的滤出物；/nS3、将滤出物与铁氧化催化剂、木炭泥、葡萄糖、小苏打混合均匀，在500-800℃的富氧条件下通过自燃充分燃烧，进行5-6小时后，烧结成具有多孔隙结构的块状体，获得三氧化二铁固化物。/n
【技术特征摘要】
1.一种红泥的处理方法，其特征在于，包括以下步骤：
S1、用洗涤水对红泥进行洗涤获得稀释液，同时在池底鼓风进行搅拌，洗涤操作持续2-3小时；
S2、将稀释液通入离心机进行固液分离操作，获得主要成分为铁金属化合物的滤出物；
S3、将滤出物与铁氧化催化剂、木炭泥、葡萄糖、小苏打混合均匀，在500-800℃的富氧条件下通过自燃充分燃烧，进行5-6小时后，烧结成具有多孔隙结构的块状体，获得三氧化二铁固化物。
2.根据权利要求1所述的红泥的处理方法，其特征在于，洗...
【专利技术属性】
技术研发人员：刘沐之，郑先强，
申请(专利权)人：北京航天国环技术有限公司，
类型：发明
国别省市：北京;11