The invention provides a new process of preparing high-performance iron oxide from iron oxide red produced by acid washing liquid of steel plant for soft magnetic materials. The process includes: adding hydrochloric acid to the reactor first, then adding the iron oxide red powder produced by acid washing liquid of steel plant to the reactor, then heating and pressing to generate iron chloride solution, entering the extraction and purification process, preparing high-purity iron chloride solution, and preparing high-performance iron chloride solution Pure ferric chloride solution was produced by roasting method with roasting method to produce 99.9% high performance iron oxide. The invention has the advantages of low leaching pressure, 99.9% recovery and utilization of hydrochloric acid, targeted purification, recycling of extractant and high performance.
【技术实现步骤摘要】
钢厂酸洗液生产的氧化铁红制备高性能氧化铁用于软磁材料的新工艺
本专利技术涉及粉体功能材料领域，具体涉及一种钢厂酸洗液生产的氧化铁红制备高性能氧化铁用于软磁材料的新工艺。
技术介绍
高性能氧化铁，是指纯度在99.6％以上的三氧化二铁，目前主要是生产软磁材料的原料，可广泛用于声电、微波、存储、通信及军工等领域，具有广泛的应用前景。软磁铁氧体所用原料中,用量最大的是氧化铁红,其占原材料总量的70％，氧化铁红的质量对生产铁氧体的性能影响极大。目前,采用的钢厂酸洗液喷雾焙烧工艺：主要以轧钢厂酸洗废液(主要化学成分是FeCL2)为原料，通过喷雾焙烧设备生产出副产品氧化铁红，只有少数大钢铁厂生产出纯度只有99.4％的氧化铁红，即使这样，氧化铁纯度低,其中含氯离子、其他重金属等杂质较高，不能制造高端产品。综上所述，现有技术中存在以上问题：采用的钢厂酸洗液喷雾焙烧工艺无法生产高性氧化铁软磁材料。
技术实现思路
本专利技术提供一种钢厂酸洗液生产的氧化铁红制备高性能氧化铁用于软磁材料的新工艺，即...
【技术保护点】
1.一种钢厂酸洗液生产的氧化铁红制备高性能氧化铁用于软磁材料的新工艺包括：/n步骤A：准备钢厂酸洗液生产的氧化铁红粉末作为原料；/n步骤B：首先向反应釜中加入盐酸，再将氧化铁红粉末加入到反应釜中，然后向反应釜加压1MPa，加温至90℃，经过150分钟的反应，生成氯化铁溶液；/n步骤C：向氯化铁溶液加入盐酸，形成盐酸浓度为5-7MoL/L的氯化铁溶液，然后进入萃取系统，经过正萃、洗涤、反萃，控制反萃液中的三价铁离子Fe
【技术特征摘要】
1.一种钢厂酸洗液生产的氧化铁红制备高性能氧化铁用于软磁材料的新工艺包括：
步骤A：准备钢厂酸洗液生产的氧化铁红粉末作为原料；
步骤B：首先向反应釜中加入盐酸，再将氧化铁红粉末加入到反应釜中，然后向反应釜加压1MPa，加温至90℃，经过150分钟的反应，生成氯化铁溶液；
步骤C：向氯化铁溶液加入盐酸，形成盐酸浓度为5-7MoL/L的氯化铁溶液，然后进入萃取系统，经过正萃、洗涤、反萃，控制反萃液中的三价铁离子Fe3+浓度为9-11％，反萃后氯化铁溶液纯度达到99.9％以上...