The invention provides a method for extracting silica from the tail slag of extracting vanadium from shale, which comprises the following steps: (1) mixing the tail slag of extracting vanadium with solid alkali and water to obtain the slag slurry, the mass ratio of the solid alkali to the tail slag of extracting vanadium is 0.9-2:1, and the solid-liquid ratio is 1:4-10; (2) raising the temperature of the slag slurry to 120 \u2103 - 180 \u2103, and controlling the reaction time to 60-150 min; (3) filtering the filtrate and Filter residue, adjust the pH value of filtrate to 6~10, get the silicon gel; (4) the silica gel is dried and ground to obtain white carbon black; the silica leaching rate of the method is up to 95.2%, and the reaction time is shortened greatly, and the reaction time is 60 to 150min, and SiO is detected in the product.
【技术实现步骤摘要】
一种从页岩提钒尾渣中提取白炭黑的方法
本专利技术涉及石煤提取及资源综合利用
，特别涉及一种从页岩提钒尾渣中提取白炭黑的方法。
技术介绍
白炭黑即非晶态二氧化硅。又名水合二氧化硅。分子式为SiO2·nH2O。是一种白色、无毒、无定型微细粉状物。具有多孔性、高分散、质轻、化学稳定性好、耐高温、不燃烧和电绝缘性好等优异性能。白炭黑在橡胶工业中主要用作补强剂和改性剂，其补强效果优于炭黑以外的其它补强填充剂。白炭黑还是塑料、造纸、农药、涂料、油墨等行业的原材料。目前白炭黑的制造方法分为气相法和沉淀法，气相法制备白炭黑产品质量好，但其成本较高、对设备的要求较高，工艺复杂；目前国内采用制备白炭黑的方法大多为沉淀法，沉淀法白炭黑产品质量不如气相法白炭黑，但是沉淀法白炭黑生产工艺简单，操作容易，成本也低。因此目前国内大部分都是采用沉淀法生产白炭黑。页岩提钒尾渣是从钒页岩中提取钒金属后产生的尾渣，钒页岩中钒的品位较低，平均每利用钒页岩生产1tV2O5产品就会产生120～150t的尾渣。大量的尾渣的堆积不仅占用土地，给企业的发展带来...
【技术保护点】
1.一种从页岩提钒尾渣中提取白炭黑的方法，其特征在于，所述方法包括如下步骤：/n步骤1、将提钒尾渣与固体碱、水混合得到渣浆，所述固体碱与提钒尾渣质量比为0.9～2：1，固液比为1：4～10；/n步骤2、将步骤1所得的渣浆升高温度至120℃～180℃，控制反应时间为60～150min；/n步骤3、反应结束后过滤得到滤液和滤渣，调节滤液pH值至6～10，得到硅凝胶；/n步骤4、将步骤3所得的硅凝胶烘干磨碎即得白炭黑。/n
【技术特征摘要】
1.一种从页岩提钒尾渣中提取白炭黑的方法，其特征在于，所述方法包括如下步骤：
步骤1、将提钒尾渣与固体碱、水混合得到渣浆，所述固体碱与提钒尾渣质量比为0.9～2：1，固液比为1：4～10；
步骤2、将步骤1所得的渣浆升高温度至120℃～180℃，控制反应时间为60～150min；
步骤3、反应结束后过滤得到滤液和滤渣，调节滤液pH值至6～10，得到硅凝胶；
步骤4、将步骤3所得的硅凝胶烘干磨碎即得白炭黑。
2.如权利要求1所述的方法，其特征在于，所述步骤1中固体碱为氢氧化钠或者氢氧化钾。
3....
【专利技术属性】
技术研发人员：包申旭，王顺，张一敏，
申请(专利权)人：武汉理工大学，
类型：发明
国别省市：湖北;42