The invention discloses a threonine modified montmorillonite, a preparation method and an application thereof. In the method, the raw material sodium montmorillonite is pretreated by acid modification, drying and sieving, and then the modifier threonine is dissolved in water and adjusted to a pH of 3-5. The pretreated acid modified sodium montmorillonite is added, the reaction is stirred at room temperature, and finally the threonine modified montmorillonite is obtained by suction filtration, washing, drying and sieving. The montmorillonite modified by the invention has good adsorption capacity for Pb (\u2161), Cu (\u2161) and other metal ions in water, and the saturated adsorption capacity can reach 120mg / g and 30mg / g respectively, which has a good application prospect in the field of heavy metal ion wastewater treatment.
【技术实现步骤摘要】
苏氨酸改性蒙脱石、制备方法及其应用
本专利技术涉及一种氨基酸改性蒙脱石、制备方法及其应用，属于改性矿物吸附材料制备及重金属废水处理
技术介绍
电子制造所涉及的电池制造行业、冶金行业，以及日常当中涉及的汽车喷涂、电镀等行业都会产生了大量的含重金属废水。重金属由于无法被动物体分解，随着生物链的进行具有极强的生物体富集效应，一旦进入人体，在长期的积累下会对人体的神经系统和肝肾脏等器官造成严重损害。传统处理含重金属废水的方法包括膜分离法、化学沉淀、离子交换法、电化学法、生物降解法和吸附法。其中从经济实用、操作便捷、去除效率等方面综合考虑，吸附法是目前工业处理含重金属离子废水常用的方法。蒙脱石是一种自然界广泛存在的硅酸盐矿物，它所具有的层状结构使其具有一定的吸附金属离子的能力。其层状构成方式为一层铝氧(Al-(O,OH))八面体夹在两层硅氧(Si-O)四面体当中，利用共有的氧原子将八面体和四面体连接起来。蒙脱石主要来源于膨润土矿，具有亲水性、耐高温、来源丰富和吸附性能良好的优点。相比于工业上常用的活性炭吸附剂...
【技术保护点】
1.苏氨酸改性蒙脱石的制备方法，其特征在于，具体步骤如下：/n步骤1，钠基蒙脱石粉末加入水中，滴加盐酸调节pH至4～6，常温搅拌12～24h，抽滤，烘干和过筛，得到酸改性钠基蒙脱石；/n步骤2，按苏氨酸与酸改性钠基蒙脱石的质量比为0.153～0.229倍钠基蒙脱石阳离子交换容量：1，将苏氨酸搅拌溶解于水中，调节溶液pH为3～5，加入酸改性钠基蒙脱石粉末，室温下搅拌，抽滤，洗涤，烘干，研磨过筛，得到苏氨酸改性蒙脱石。/n
【技术特征摘要】
1.苏氨酸改性蒙脱石的制备方法，其特征在于，具体步骤如下：
步骤1，钠基蒙脱石粉末加入水中，滴加盐酸调节pH至4～6，常温搅拌12～24h，抽滤，烘干和过筛，得到酸改性钠基蒙脱石；
步骤2，按苏氨酸与酸改性钠基蒙脱石的质量比为0.153～0.229倍钠基蒙脱石阳离子交换容量：1，将苏氨酸搅拌溶解于水中，调节溶液pH为3～5，加入酸改性钠基蒙脱石粉末，室温下搅拌，抽滤，洗涤，烘干，研磨过筛，得到苏氨酸改性蒙脱石。
2.根据权利要求1所述的制备方法，其特征在于，步骤1中，所述的钠基蒙脱石的阳离子交换容量为70～110mmoL/100g。