The invention discloses a cobalt oxide nanocrystal and a preparation method and application thereof. The preparation method comprises the following steps: dissolving cobalt source, alkali and / or ethanol in water and mixing evenly; then putting the mixed solution into an environment of 180 \u2011 220 \u2103 for reaction for 5 \u2011 7h, centrifuging after the reaction and drying the collected product; carrying out gradient heating treatment on the dried product and heating up The final product was obtained at a speed of 0.8 \u2011 1.2 \u2103 / min and a final heating temperature of 330 \u2011 370 \u2103. The preparation method is simple and easy, and the nano cube with exposed surface of {110} and the nano sheet with exposed surface of {112} can be prepared. The nano cube and nano sheet have high catalytic activity.
【技术实现步骤摘要】
四氧化三钴纳米晶及其制备方法与应用
本专利技术属于无机纳米材料制备领域，具体涉及一种四氧化三钴纳米晶及其制备方法与应用。
技术介绍
公开该
技术介绍
部分的信息仅仅旨在增加对本专利技术的总体背景的理解，而不必然被视为承认或以任何形式暗示该信息构成已经成为本领域一般技术人员所公知的现有技术。纳米晶因其独特的性质广泛应用于各种催化领域。不同形状的纳米晶催化剂通常会暴露不同的晶面，因此表现出不同的催化吸附能力。从这一角度出发，调控晶面也是一种提高催化活性的策略。例如，BiVO4纳米晶的(040)晶面在太阳能转化方面能够提供更多的光催化活性位点；BiOI的(110)晶面比(001)晶面在水溶液中能够产生更多的O2·-和·OH自由基，从而表现出更高的催化降解有机污染物的能力，因此控制合成具有高活性晶面的纳米催化剂具有重要意义。Co3O4因其在催化、超级电容器、锂离子电池及气敏等领域的应用引起了广大科研工作者的关注。Co3O4纳米材料的制备方法主要有高温热分解法、氧化还原法、电化学沉积法等，大部分的方法是先制备出前驱体，煅烧...
【技术保护点】
1.一种四氧化三钴纳米晶的制备方法，其特征在于：包括如下步骤：/n将钴源、碱和/或乙醇溶于水中，混合均匀；然后将混合溶液放入180-220℃的环境中反应5-7h，反应完毕后，离心，将收集到的产物干燥；/n将干燥后的产物进行梯度升温处理，升温速度为0.8-1.2℃/min，最终加热温度为330-370℃，并保温一定时间，得最终产物。/n
【技术特征摘要】
1.一种四氧化三钴纳米晶的制备方法，其特征在于：包括如下步骤：
将钴源、碱和/或乙醇溶于水中，混合均匀；然后将混合溶液放入180-220℃的环境中反应5-7h，反应完毕后，离心，将收集到的产物干燥；
将干燥后的产物进行梯度升温处理，升温速度为0.8-1.2℃/min，最终加热温度为330-370℃，并保温一定时间，得最终产物。
2.根据权利要求1所述的四氧化三钴纳米晶的制备方法，其特征在于：所述钴源为Co(NO3)2。
3.根据权利要求1所述的四氧化三钴纳米晶的制备方法，其特征在于：制备四氧化三钴立方块时，采用的原料为钴源、氨水和乙醇。
4.根据权利要求3所述的四氧化三钴纳米晶的制备方法，其特征在于：反应液中Co(NO3)2的浓度范围为0.08-0.12mol/L；
进一步的，反应液中氨水的浓度范围为1.8-2.0mol/L；
进一步的，溶剂中水和乙醇的体积比范围为1:3-1:4。
5.根据权利要求1所述的四氧化...