The present invention relates to a metal salt fog rust-proof liquid. The components of the metal salt fog rust-proof liquid are as follows: dimethyl carbonate 30 40, hexamethylphosphoryltrimide 20 25, polycarbonate 10 15, zinc borate 10 15, borosilicate 5 10, dioctyl phthalate 5 10, caprolactam blocked aromatic polyisocyanate 5 10, decay. Potassium phytate 1_6, dispersant 3_5, cosolvent 4_6, thickener 0.5_1, diluent 35_45. The metal rust-proof liquid of the invention has strong salt fog resistance, can form a dense protective film on the metal surface of copper, iron and stainless steel, effectively prevent external material from corroding metal, does not affect conductive welding, and the protective film is easy to clean.
【技术实现步骤摘要】
一种五金耐盐雾防锈液
本专利技术涉及五金防锈
,尤其涉及一种五金耐盐雾防锈液。
技术介绍
金属表面防锈是工业生产中的重要课题,传统的防锈液、防锈油有优点也有缺点。普通防锈水中含大量的亚硝酸钠,有致癌性,不利于环保和人身体健康,而采用保湿剂延长防锈水的寿命,又带来沾手、沾灰尘的弊病,且不能长期防锈;一般硬膜防锈油虽然适合长期防锈,成膜也透明美观,但是无色透明的树脂种类较少,不稳定也易氧化变色,还需要有机溶剂溶解,带来易燃易爆的危险也不利于环保和健康;一般的防锈油使用矿物油,难降解,而且用于短期防锈时也会带来除油难的问题。因此,研究综合性能更加优异,针对不同场合研究更加适合的防锈产品是新的方向和趋势。
技术实现思路
为解决上述问题,本专利技术提供了一种五金耐盐雾防锈液。本专利技术的技术方案如下:一种五金耐盐雾防锈液,所述五金耐盐雾防锈液的组分按照重量份如下所示:碳酸二甲酯30-40份,六甲基磷酰三胺20-25份,聚碳酸酯10-15份,硼酸锌10-15份,硼聚硅酸酯5-10份,邻苯二甲酸二辛酯5-10份,己内酰胺封闭型芳香族多异氰酸酯5-10份,腐植酸钾1-6份、分散剂3-5份、助溶剂4-6份,增稠剂0.5-1份、稀释剂35-45份。进一步的,所述分散剂为十二烷基硫酸钠、1,6-己二醇双丙烯酸酯、甲基戊醇和三乙基己基磷酸中的一种或几种混合。进一步的,所述助溶剂为乙酰胺、苯甲酸钠和对氨基苯甲酸中的一种。进一步的,所述增稠剂为海藻酸丙二醇酯、藻酸丙二醇酯和羟丙基二淀粉磷酸酯中的一种。进一步的,所述稀释剂为苯乙烯、乙酸乙酯中的一种。借由上述方案,本专利技术至少具有如 ...
【技术保护点】
1.一种五金耐盐雾防锈液,其特征在于:所述五金耐盐雾防锈液的组分按照重量份如下所示:碳酸二甲酯30‑40份,六甲基磷酰三胺20‑25份,聚碳酸酯10‑15份,硼酸锌10‑15份,硼聚硅酸酯5‑10份,邻苯二甲酸二辛酯5‑10份,己内酰胺封闭型芳香族多异氰酸酯5‑10份,腐植酸钾1‑6份、分散剂3‑5份、助溶剂4‑6份,增稠剂0.5‑1份、稀释剂35‑45份。
【技术特征摘要】
1.一种五金耐盐雾防锈液,其特征在于:所述五金耐盐雾防锈液的组分按照重量份如下所示:碳酸二甲酯30-40份,六甲基磷酰三胺20-25份,聚碳酸酯10-15份,硼酸锌10-15份,硼聚硅酸酯5-10份,邻苯二甲酸二辛酯5-10份,己内酰胺封闭型芳香族多异氰酸酯5-10份,腐植酸钾1-6份、分散剂3-5份、助溶剂4-6份,增稠剂0.5-1份、稀释剂35-45份。2.根据权利要求1所述的一种五金耐盐雾防锈液,其特征在于:所述分...
【专利技术属性】
技术研发人员:刘云鹏,
申请(专利权)人:常州德瑞电子有限公司,
类型:发明
国别省市:江苏,32