The invention uses a treatment solution of an adhesive resin to prevent rust on threaded parts such as bolts. The adhesive resin comprises at least one of the modified epoxy resins obtained by grafting polymerization with an acrylic polymer containing carboxylic acid as a side chain, or at least one of the modified acrylic resins obtained by grafting polymerization with an acrylic polymer containing carboxylic acid as a side chain, and dioxide. Silicide. If the solution is used, there is no need for organic solvents and the coating process can be carried out in one step. It has the advantage that the friction coefficient will not increase even if it is tightened repeatedly.
【技术实现步骤摘要】
【国外来华专利技术】螺纹部件用防锈处理液、经过防锈处理的螺纹部件的制造方法及经过防锈处理的螺纹部件
本专利技术涉及用于制造防锈特性优异的螺栓、螺母等螺纹部件的技术，更详细而言，涉及螺纹部件用防锈处理液、经过防锈处理的螺纹部件的制造方法及经过防锈处理过的螺纹部件。
技术介绍
例如汽车的悬架等悬架部件由于在行驶中频繁与水接触，所以对用于此类部分的螺栓、螺母等螺纹部件，要求优异的防锈性能。通常，这种螺纹部件如图1所示在铁基体1的表面形成镀锌层2来使其具有防锈性能。但是，由于镀锌层2在反复进行紧固时摩擦系数会逐渐增加，所以，如果继续该状态将无法进行稳定的紧固连结。为此，如图2所示，在镀锌层2的表面形成以蜡为主体的摩擦系数稳定层3，即使反复进行紧固，摩擦系数也不会增加。但是，包括镀锌层2与摩擦系数稳定层3的被覆层易受损，有时因与水接触而生锈。有可能出现如下情况：氢从锈部进入铁基体1的内部，由氢脆所导致的滞后破坏加剧而导致螺栓折损。为了解决该问题，如图3所示，在镀锌层2的表面形成防锈剂层4，进而在其表面形成摩擦系数稳定层3。但是，由于需要形成防锈剂层4和形成摩擦系数稳定层2这样两次涂布处理，所以...
【技术保护点】
1.一种螺纹部件用防锈处理液，其特征在于，所述螺纹部件用防锈处理液使用含有改性环氧树脂或改性丙烯酸树脂中的至少一种、和二氧化硅的粘合剂树脂，所述改性环氧树脂以含有羧酸的丙烯酸聚合物为侧链进行接枝聚合而得到，所述改性丙烯酸树脂以含有羧酸的丙烯酸聚合物为侧链进行接枝聚合而得到。
【技术特征摘要】
【国外来华专利技术】2016.08.04 JP 2016-1538391.一种螺纹部件用防锈处理液，其特征在于，所述螺纹部件用防锈处理液使用含有改性环氧树脂或改性丙烯酸树脂中的至少一种、和二氧化硅的粘合剂树脂，所述改性环氧树脂以含有羧酸的丙烯酸聚合物为侧链进行接枝聚合而得到，所述改性丙烯酸树脂以含有羧酸的丙烯酸聚合物为侧链进行接枝聚合而得到。2.如权利要求1所述的螺纹部件用防锈处理液，其特征在于，所述粘合剂树脂含有所述改性环氧树脂与所述二氧化硅，改性环氧树脂在该粘合剂树脂中的比例为20～40质量％。3.如权利要求2所述的螺纹部件用防锈处理液，其特征在于，所述螺纹部件用防锈处理液含有所述粘合剂树脂与蜡。4.如权利要求1所述的螺纹部件用防锈处理液，其特征在于，所述粘合剂树脂含有所述改性丙烯酸树脂与所述二氧化硅，改性丙烯酸树脂在该粘合剂树脂中的比例为20～40质量％。5.一种经过防锈处理的螺纹部件的制造方法，其特征在于，具有下述工序:在螺纹部件的表面形成耐腐蚀膜的工序；在该耐腐蚀膜的表面涂布防锈处理液形成防...