一种橡胶防老剂制造技术

本发明专利技术提供一种橡胶防老剂，包括以下组分：聚丁基双酚、乙烯化苯酚、三（壬基苯基）亚磷酸酯、歧化松香酸钾皂、抗氧剂、催化剂、二甲苯甲醛树脂和硅烷偶联剂，本发明专利技术的橡胶防老化剂，其毒性降低，杂质含量低，迁移率低。且其制备工艺简单，价格便宜，可降低成本，提高产品质量和经济效益。本发明专利技术能有效减少防老剂迁移产生的环境污染，在橡胶材料中分散性好，实用效果高。

A rubber antioxidant

The invention provides a rubber antioxidant, which comprises the following components: polybutyl bisphenol, vinylated phenol, tri (nonylphenyl) phosphite, disproportionated potassium rosinate soap, antioxidant, catalyst, xylene formaldehyde resin and silane coupling agent. The rubber antioxidant of the invention has low toxicity, low impurity content and low mobility. The preparation process is simple, the price is cheap, the cost can be reduced, and the product quality and economic benefits can be improved. The invention can effectively reduce the environmental pollution caused by the migration of antioxidant, has good dispersion in rubber materials and high practical effect.

【技术实现步骤摘要】
一种橡胶防老剂
本专利技术涉及一种防老剂，特别涉及一种橡胶防老剂。
技术介绍
橡胶及其制品在加工、贮存和使用过程中，由于受到内外因素，会逐渐发粘、变硬发脆或龟裂。这种物理机械性能随时间而下降、弹性降低的现象叫做老化。随着老化过程的进行和发展，橡胶及其制品性能会逐渐降低以致完全丧失使用价值。为此，需在橡胶及其制品中加入某些化学物质来提高它对上述各种破坏作用的抵抗能力，延缓或抑制老化过程，从而延长橡胶及其制品的贮存期和使用寿命。目前市面上的防老剂使用壬基酚类防老剂，具有内分泌干扰效应，可促进乳腺癌细胞增殖，属于内分泌干扰物，致癌物，壬基酚类防老剂的使用，不仅大大制约橡胶的使用量和使用范围而且会产生不利于环保的有害物质。防老剂在20世纪30年代就开始生产应用，由于其能有效地防护热氧老化和屈挠疲劳引起的老化，且价格低廉，因此在橡胶工艺中用量很大。但现有的很多橡胶防老剂存在毒性，且贮存稳定性差，暴露在空气中及日光下就会由白色变为灰黑色。子啊橡胶产品使用过程中，尤其是在热和光的作用下，透明橡胶会变为深色，同时通过迁移来污染与其接触的材料。
技术实现思路
本专利技术为了弥补现有技术的不足，提供了一种橡本文档来自技高网...

【技术保护点】
1.一种橡胶防老剂，其特征在于，包括以下组分：以重量组分计，聚丁基双酚5‑20份，乙烯化苯酚3‑15份，三（壬基苯基）亚磷酸酯35‑50份，歧化松香酸钾皂4‑9份，抗氧剂15‑38份，催化剂4‑10份，二甲苯甲醛树脂5‑8份和硅烷偶联剂2‑8份。

【技术特征摘要】
1.一种橡胶防老剂，其特征在于，包括以下组分：以重量组分计，聚丁基双酚5-20份，乙烯化苯酚3-15份，三（壬基苯基）亚磷酸酯35-50份，歧化松香酸钾皂4-9份，抗氧剂15-38份，催化剂4-10份，二甲苯甲醛树脂5-8份和硅烷偶联剂2-8份。2.根据权利要求1所述的橡胶防老剂，其特征在于，以重量组分计包括以下组分：抗氧剂25-33份，聚丁基双酚8-10份，三（壬基苯基）亚磷酸酯42-45份，歧化松香酸钾皂5-8份，催化剂5-7份，乙烯化苯酚5-8份，二甲苯甲醛树脂6-7份，硅烷...