The invention relates to a processing method of fiber-reinforced foam glass. The fiber reinforced foam glass is mainly made from the following raw materials: fiber reinforced 60 parts, 80 parts, Glauber's salt 2, 4 parts, calcium carbonate 1, 3 parts, iron oxide 1, 3 parts, graphite 2, 4 parts. The mould box is made of preheated, sintered, foamed, stabilized foam, stereotyped, demoulding, annealed and cooled foam glass blanks; the blank is cut into finished products; the foam glass of the invention has uniform gas phase and solid phase system, the strength of the foam glass is high, the process operation is simple, the manufacturing cost is low, and the energy saving and environmental protection are achieved.
【技术实现步骤摘要】
一种纤维增强泡沫玻璃的加工方法
本专利技术涉及泡沫玻璃加工领域，尤其是涉及纤维增强泡沫玻璃的加工方法。
技术介绍
近年来，随着人们环保意识的不断增强及自然资源的紧缺，废玻璃等工业废渣资源化循环利用日益受到重视。泡沫玻璃是利用废玻璃制造的多孔材料，内部充满无数小气泡，它的性质不同于普通玻璃，具有强度高、密度小、导热系数小、使用寿命长、易加工可锯切等优点，是一种性能良好的保温隔热和吸声的节能环保材料，广泛用作建筑工程、冷冻装置、热工设备等领域。为了减少工业废弃物的污染、噪音污染，加强工业固废的资源化综合利用，发展循环经济，是我国实现可持续发展的迫切需求。
技术实现思路
本专利技术的目的是为了提供一种纤维增强泡沫玻璃的加工方法。为了实现上述目的，本专利技术采用了如下技术方案：一种纤维增强泡沫玻璃的加工方法，纤维增强泡沫玻璃按重量份数主要由如下原料制备得到：玻璃碎渣60-80份、芒硝2-4份、乙二胺盐2-4份，三氧化二铝2-4份、磷酸钠1-3份、碳纤维1-3份、玻璃纤维1-3份；包括如下步骤：将上述原料混合均匀球磨制得500目以下细粉；将所述细粉装入耐热钢模盒，经预热、烧结、...
【技术保护点】
1.一种纤维增强泡沫玻璃的加工方法，其特征在于，纤维增强泡沫玻璃按重量份数主要由如下原料制备得到：玻璃碎渣60‑80份、芒硝2‑4份、乙二胺盐2‑4份，三氧化二铝2‑4份、磷酸钠1‑3份、碳纤维1‑3份、玻璃纤维1‑3份；包括如下步骤：将上述原料混合均匀球磨制得500目以下细粉；将所述细粉装入耐热钢模盒，经预热、烧结、发泡、稳泡、定型、脱模、退火、冷却制得泡沫玻璃毛坯；将毛坯切割成为成品。
【技术特征摘要】
1.一种纤维增强泡沫玻璃的加工方法，其特征在于，纤维增强泡沫玻璃按重量份数主要由如下原料制备得到：玻璃碎渣60-80份、芒硝2-4份、乙二胺盐2-4份，三氧化二铝2-4份、磷酸钠1-3份、碳纤维1-3份、玻璃纤维1-3份；包括如下步骤：将上述原料混合均匀球磨制得500目以下细粉；将所述细粉装入耐热钢模盒，经预热、烧结、发泡、稳泡、定型、脱模、退火、冷却制得泡沫玻璃毛坯；将毛坯切割成为成品。2.根据权利要求1所述的一种纤维增强泡沫玻璃的加工方法，其特征在于，所述预热为在室温至400℃时，升温速度为5～10℃...