The invention relates to a preparation method of a single atom Au modified CeO 2 (Au/CeO 2) catalyst for formaldehyde degradation at low temperature. The main preparation steps are as follows: step 1, weighing appropriate amount of mesoporous CeO 2 powder in deionized water; step 2, configuring Au precursor solution; step 3, slowly injecting Au precursor solution into CeO 2 solution by using a microinjection pump; step 4, injecting mixed solution into CeO 2 solution; The process of magnetic stirring, stationary, centrifugal and drying is carried out. The U/CeO 2 catalyst prepared by the invention exhibits excellent catalytic degradation performance for formaldehyde at about 45 C.
【技术实现步骤摘要】
一种低温降解甲醛的单原子Au改性CeO2催化剂的制备方法
本专利技术涉及化工及环保领域，具体涉及一种低温降解甲醛单原子Au改性CeO2(Au/CeO2)催化剂的制备方法。
技术介绍
随着环境污染现象的日益加重,空气质量问题引起了人们的极度重视。而沸点在50℃～260℃，室温下饱和蒸汽压大于133.3Pa的可挥发性有机化合物(VOCs)是污染环境、影响人们健康的主要污染源。其中，甲醛作为日常生活中最常见的可挥发性有机污染物，与人体的身心健康密切相关。研究低温可高效降解甲醛的催化剂具有重要意义。由于CeO2中存在着Ce3+而具有独特的化学结构，存在着储氧和释放氧的能力，较强的氧化还原能力(Ce4+/Ce3+)，因此，CeO2是一种很好的热催化剂。针对CeO2催化降解VOCs的研究得到了广大学者的追捧。但是，由于CeO2热催化降解VOCs的起燃温度普遍较高，通常在120℃以上，能量消耗较高，使其应用受到了限制。研究者多会采取贵金属改性的办法来修饰CeO2材料，进而降低其热催化降解VOCs的起燃温度。近年来，许多研究者致力于贵金属Au改性CeO2材料降解甲醛的研究。但以往...
【技术保护点】
1.一种低温降解甲醛的单原子Au改性CeO2催化剂的制备方法，其特征在于包括以下步骤：步骤一、称量介孔CeO2粉末于水中搅拌均匀，得到介孔CeO2水溶液；步骤二、配置HAuCl4水溶液，作为Au前驱体溶液；步骤三、使用微量注射泵将Au前驱体溶液缓慢注射到均匀的介孔CeO2水溶液中，搅拌反应后，得到均匀的混合液；其中，注射速率为(0.01~1) ml/min；步骤四、将步骤三所得混合液经静置、过滤、超声清洗、离心、干燥后，得到单原子Au改性CeO2催化剂。
【技术特征摘要】
1.一种低温降解甲醛的单原子Au改性CeO2催化剂的制备方法，其特征在于包括以下步骤：步骤一、称量介孔CeO2粉末于水中搅拌均匀，得到介孔CeO2水溶液；步骤二、配置HAuCl4水溶液，作为Au前驱体溶液；步骤三、使用微量注射泵将Au前驱体溶液缓慢注射到均匀的介孔CeO2水溶液中，搅拌反应后，得到均匀的混合液；其中，注射速率为(0.01~1)ml/min；步骤四、将步骤三所得混合液经静置、过滤、超声清洗、离心、干燥后，得到单原子Au改性CeO2催化剂。2.根据权利要求1所述的一种低温降解甲醛的单原子Au改性CeO2催化剂的制备方法，其特征在于步骤一中，介孔CeO2粉末为立方萤石相，介孔孔径大小为1.1~1.5nm。3.根据权利要求1所述的一种低温降解甲醛的单原子Au改性CeO2催化剂的制备方法，其特征在于步骤一中，介孔CeO2水溶液浓度在0.06~0.3mol/L范围内。4.根据权利要求1所述的一种低温降解甲醛的单原子Au改性CeO2催化剂的制备方法，其特征...