The invention provides a method for recovering arsenic, iron and calcium from arsenic, iron and calcium slag. Firstly, the arsenic, iron and calcium slag is put into the reactor, and carbon powder is added to stir sufficiently to obtain the mixture of the two. Then, the mixture is pressed into lumps in the high-pressure pellet machine, and then vacuum reduction reaction is carried out in the high-temperature vacuum furnace, and the metal arsenic is distilled to obtain the solid product, and finally magnet is used for the obtained solid product Iron powder and calcium oxide are separated by adsorption, then iron powder is washed and dried to obtain metal iron. The vacuum degree of the vacuum furnace is 10.
【技术实现步骤摘要】
一种从砷铁钙渣中回收砷铁钙的方法
本专利技术涉及金属冶炼领域，具体涉及一种从砷铁钙渣中回收砷铁钙的方法。
技术介绍
砷铁钙是一种砷酸盐矿物，砷铁钙石为单斜晶系，颜色为金黄、黄褐、红褐、褐黑到黑色，半金属光泽或丝绢光泽，呈纤维状或者硬度稍低，砷铁钙中含有砷、铁、钙等元素，在金属冶炼过程中，若将将砷铁钙渣直接丢弃，不仅浪费资源，增加劳动成本，而且会污染环境，不能满足绿色生产的要求，因此，需要对砷铁钙渣进行回收利用，提高资源利用效率，减少环境污染。
技术实现思路
为解决上述问题，本专利技术提供一种从砷铁钙渣中回收砷铁钙的方法，具体步骤如下：（1）将砷铁钙渣置入反应器内，加入碳粉后进行充分搅拌，得到二者的混合物；（2）将步骤（1）得到的混合物在高压制团机中压成块，然后置于高温真空炉中进行真空还原反应，并蒸馏得到金属砷；（3）对步骤（2）得到的固体生成物进行磁铁吸附对铁粉和氧化钙进行分离，再对铁粉进行洗涤、干燥后即得到金属铁。所述步骤（2）中的真空炉的真空度为10-3~10-2mmHg。相对于现有技术，本专利技术的有益效果为：通过对砷铁钙渣中的进行钙、铁、砷回收利用，不仅提高了资源利用效率，降低了成产成本，而且减少了环境污染，满足了绿色生产的要求。附图说明图1为本专利技术的工艺流程图。具体实施方式下面将结合本专利技术实施例中的附图，对本专利技术实施例中的技术方案进行清楚、完整地描述。实施例：本专利技术提供一种从砷铁钙渣中回收砷铁钙的方法，具体步骤如下：（1）将砷铁钙渣置入反应器内，加入碳粉后进行充分搅拌，得到二者的混合物；（2）将步骤（1）得到的混合物在高压制团机中压成...
【技术保护点】
1.一种从砷铁钙渣中回收砷铁钙的方法，其特征在于，具体步骤如下：（1）将砷铁钙渣置入反应器内，加入碳粉后进行充分搅拌，得到二者的混合物；（2）将步骤（1）得到的混合物在高压制团机中压成块，然后置于高温真空炉中进行真空还原反应，并蒸馏得到金属砷；（3）对步骤（2）得到的固体生成物进行磁铁吸附对铁粉和氧化钙进行分离，再对铁粉进行洗涤、干燥后即得到金属铁。
【技术特征摘要】
1.一种从砷铁钙渣中回收砷铁钙的方法，其特征在于，具体步骤如下：（1）将砷铁钙渣置入反应器内，加入碳粉后进行充分搅拌，得到二者的混合物；（2）将步骤（1）得到的混合物在高压制团机中压成块，然后置于高温真空炉中进行真空还原反应，并蒸馏得到金属...
【专利技术属性】
技术研发人员：卢建中，
申请(专利权)人：济源市中亿科技有限公司，
类型：发明
国别省市：河南,41