The invention relates to a production process of one-way perspective film. It includes the following steps: (1) preparing master batch by using EVA resin with melting index of 3 5g/10min at 190 (?) and polymer wax as dispersant; (2) mixing master batch with EVA resin and coupling agent evenly, the content of VA in EVA resin is 30 33%, and the melting index is less than 1g/10min at 190 (?) forming one-way perspective film by tape casting process. In this step, the extrusion volume of the extruder is controlled at 100 120 kg/h, the screw temperature of the extruder is controlled at 115 130, the sleeve temperature is controlled below 130, and the die temperature is controlled at 130 145.
【技术实现步骤摘要】
一种单向透视胶片的生产工艺
本专利技术涉及一种单向透视胶片的生产工艺。
技术介绍
在建筑装饰等领域，夹胶玻璃以其美观、坚固等优良特性得到了越来越广泛的应用，夹胶玻璃包括位于中心的玻璃胶片层和位于两侧的玻璃。单向透视玻璃是一款将液晶膜复合进两层玻璃中间，经高温高压胶合后，一体成型的夹层结构的新型特种光电玻璃产品，具有单向透视的特性。单向透视胶片在现有加工工艺下不利于生产。
技术实现思路
本专利技术为解决公知技术中存在的技术问题而提供一种单向透视胶片的生产工艺，解决
技术介绍
中存在的问题。本专利技术为解决公知技术中存在的技术问题所采取的技术方案是：一种单向透视胶片的生产工艺包括以下步骤，(1)制备母粒的步骤，母粒基材采用190℃时熔融指数在3-5g/10min的EVA树脂，采用高分子蜡作分散剂；(2)将母粒与EVA树脂和偶联剂混合均匀的步骤，EVA树脂的VA含量为30-33％，在190℃时熔融指数小于1g/10min；(3)采用流延成膜工艺生成单向透视胶片的步骤，此步骤时挤出机的挤出量控制在100-120kg/h，挤出机的螺杆温度控制在115℃-130℃，套筒温度控制在130℃以下，模头温度控制在130℃-145℃本专利技术的优点和积极效果是：本专利技术提供了一种单向透视胶片的生产工艺，通过采用EVA材料代替传统的PVB材料，在生产过程中采用了低温成型工艺，得到的胶片具有单向透光的特性。优选地：步骤(2)中所述的偶联剂选取为氨丙基三甲氧基硅烷或者氨乙基氨丙基三乙氧基硅烷。优选地：步骤(3)中流延成膜工艺采用单螺杆挤出机，挤出温度为90℃-130℃。具体实施方式为能进...
【技术保护点】
1.一种单向透视胶片的生产工艺，其特征是：包括以下步骤，(1)制备母粒的步骤，母粒基材采用190℃时熔融指数在3‑5g/10min的EVA树脂，采用高分子蜡作分散剂；(2)将母粒与EVA树脂和偶联剂混合均匀的步骤，EVA树脂的VA含量为30‑33％，在190℃时熔融指数小于1g/10min；(3)采用流延成膜工艺生成单向透视胶片的步骤，此步骤时挤出机的挤出量控制在100‑120kg/h，挤出机的螺杆温度控制在115℃‑130℃，套筒温度控制在130℃以下，模头温度控制在130℃‑145℃。
【技术特征摘要】
1.一种单向透视胶片的生产工艺，其特征是：包括以下步骤，(1)制备母粒的步骤，母粒基材采用190℃时熔融指数在3-5g/10min的EVA树脂，采用高分子蜡作分散剂；(2)将母粒与EVA树脂和偶联剂混合均匀的步骤，EVA树脂的VA含量为30-33％，在190℃时熔融指数小于1g/10min；(3)采用流延成膜工艺生成单向透视胶片的步骤，此步骤时挤出机的挤出量控制在100-12...
【专利技术属性】
技术研发人员：崔九峰，
申请(专利权)人：天津三瑞塑胶制品有限公司，
类型：发明
国别省市：天津,12