A demoulding agent for polishing Brass Ingot Casting demoulding is characterized by: the mass percentage of the components of the demoulding agent is: graphite 94%-98%, carboxymethyl cellulose 0.1%-1.0%, sodium methylenedinaphthalene sulfonate 0.1%-1.5%, SDS foaming powder 0.1%-1.0%, borax decahydrate 1%-4%, and other impurities. The formulation of the present invention is scientific and reasonable, and the preparation method is simple. Only the raw materials are stirred uniformly, and the slurry of release agent with a concentration of 13%-15% is prepared by stirring with warm water of 80-100 degrees Celsius. It has the characteristics of good release effect, convenient use, safety and harmlessness. Spraying the release agent prepared by the present invention on the mould can obviously improve the smoothness of the ingot and the damage process of the mould. Degree has been effectively reduced.
【技术实现步骤摘要】
一种抛光黄铜锭浇铸脱模用的脱模剂及其制备方法
本专利技术属于化工冶金
，涉及一种脱模剂，尤其涉及一种抛光黄铜锭浇铸脱模用的脱模剂及其制备方法。
技术介绍
抛光黄铜锭包括普通铅黄铜，硅无铅黄铜，铋无铅黄铜等，其中铅黄铜具有极高的切削性，优异的冷热铸造性能，切削易碎，加工工件表面光洁，被广泛的用于电子电讯、家电、五金饰品以及卫浴水暖产品，抛光铅黄铜在卫浴水暖产品中使用量非常大，随着生活水平的提高以及技术的进步，开始对生活质量要求不断提高，水暖卫浴产品使用材料中的铅对人体存在危害，所以开发出硅无铅，铋无铅黄铜来替代中高端铅黄铜卫浴产品。抛光黄铜被广泛用于生活中的水暖卫浴产品，主要包括水阀，花洒，水管，闸阀，球阀，各式水龙头等产品，生产工序为型材机加工路线和热锻机加工路线，其中型材机加工路线：配料-熔炼-浇铸-铸锭打包-二次熔炼-型材-机加工-表面电镀处理；热锻机加工路线：配料-熔炼-浇铸-铸锭打包-二次熔炼-型材-热锻-切边-抛丸-机加工-表面电镀处理。上述加工过程中浇铸工序需要起模，起模的好坏直接关系到铸锭质量好坏，以及二次熔炼质量，最终体现在铸锭抛光杂质点的多...
【技术保护点】
1.一种抛光黄铜锭浇铸脱模用的脱模剂，其特征在于：所述脱模剂的成分的质量百分比为：石墨94％～98％，羧甲基纤维素0.1％～1.0％，亚甲基二萘磺酸钠0.1％～1.5％，SDS发泡粉0.1％～1.0％，十水硼砂1％～4％，余量为其他杂质。
【技术特征摘要】
1.一种抛光黄铜锭浇铸脱模用的脱模剂，其特征在于：所述脱模剂的成分的质量百分比为：石墨94％～98％，羧甲基纤维素0.1％～1.0％，亚甲基二萘磺酸钠0.1％～1.5％，SDS发泡粉0.1％～1.0％，十水硼砂1％～4％，余量为其他杂质。2.根据权利要求1所述的脱模剂，其特征在于：所述石墨为鳞片石墨，粒径2000目。3.根据权利要求2所述的脱模剂，其特征在于：所述脱模剂的成分的质量百分比为：石墨94％～98％，羧甲基纤维素0.1％～0.8％，亚甲基二萘磺酸钠0.1％～1.2％，SDS发泡粉0.3％～1.0％，十水硼砂1％～3.5％。4.根据权利要求3所述的脱模...
【专利技术属性】
技术研发人员：欧阳好，
申请(专利权)人：宁波金田铜业集团股份有限公司，
类型：发明
国别省市：浙江,33