A flame retardant acrylic pressure sensitive adhesive and its preparation method include isooctyl acrylate, vinyl acetate, hydroxyethyl acrylate, glycidyl acrylate, azodiisobutyronitrile and ethyl acetate. The flame retardant of acrylate polymer is halogen-free flame retardant, and the mass fraction of halogen-free flame retardant is 5-10 phr. The mass fraction of each component is 50-80 phr of isooctyl acrylate and acetic acid. Ethylene ester 10-30 phr, hydroxyethyl acrylate 1-10 phr, glycidyl acrylate 0.2-2 phr, azodiisobutyronitrile 0.2 phr and ethyl acetate 150 phr. Compared with the traditional technology, the invention adds different amount of flame retardant with little effect on peeling force. In order to achieve flame retardant effect, adding a large number of flame retardants, although it has an impact on peeling force, it can still maintain a high peeling force.
【技术实现步骤摘要】
一种阻燃丙烯酸压敏胶及其制作方法
本专利技术涉及化工领域,具体涉及一种阻燃丙烯酸压敏胶及其制作方法。
技术介绍
压敏胶应用于日常生活的各个领域,不同领域对压敏胶有着不同的要求。在电工电子,包装印刷线路用的压敏胶带,标签等一般需要具有阻燃效果。另外阻燃胶带在航天航空领域也有着广泛的用途。对于无卤阻燃的压敏胶胶水,为了达到了良好的阻燃效果,通常要加入大量的阻燃剂,但是加入阻燃剂后,胶水的剥离力会受到很大的影响。如专利CN103865449B中介绍的阻燃胶水,虽然剥离力可以超过10牛/英寸,但是自熄时间在10秒左右,不能达到很多客户要求的低于5秒的要求;又如专利CN101805567A中介绍的阻燃胶水,虽然自熄时间在5秒以下,剥离力只能达到5牛/英寸的强度。为了解决上述问题,我们做出了一系列改进。
技术实现思路
本专利技术的目的在于,提供一种阻燃丙烯酸压敏胶及其制作方法,以克服现有技术所存在的上述缺点和不足。一种阻燃丙烯酸压敏胶,其特征在于,所述丙烯酸压敏胶为丙烯酸酯聚合物,包括:丙烯酸异辛酯、醋酸乙烯酯、丙烯酸羟乙酯、丙烯酸缩水甘油酯、偶氮二异丁腈和乙酸乙酯,所述丙烯酸酯 ...
【技术保护点】
1.一种阻燃丙烯酸压敏胶,其特征在于,所述丙烯酸压敏胶为丙烯酸酯聚合物,包括:丙烯酸异辛酯、醋酸乙烯酯、丙烯酸羟乙酯、丙烯酸缩水甘油酯、偶氮二异丁腈和乙酸乙酯,所述丙烯酸酯聚合物的阻燃剂为无卤阻燃剂,所述无卤阻燃剂的质量份数为5~10份;其各组分的质量份数为:丙烯酸异辛酯50~80份醋酸乙烯酯10~30份丙烯酸羟乙酯1~10份丙烯酸缩水甘油酯0.2~2份偶氮二异丁腈0.2份乙酸乙酯150份。
【技术特征摘要】
1.一种阻燃丙烯酸压敏胶,其特征在于,所述丙烯酸压敏胶为丙烯酸酯聚合物,包括:丙烯酸异辛酯、醋酸乙烯酯、丙烯酸羟乙酯、丙烯酸缩水甘油酯、偶氮二异丁腈和乙酸乙酯,所述丙烯酸酯聚合物的阻燃剂为无卤阻燃剂,所述无卤阻燃剂的质量份数为5~10份;其各组分的质量份数为:丙烯酸异辛酯50~80份醋酸乙烯酯10~30份丙烯酸羟乙酯1~10份丙烯酸缩水甘油酯0.2~2份偶氮二异丁腈0.2份乙酸乙酯150份。2.根据权利要求1所述的一种阻燃丙烯酸压敏胶,其特征在于,所述丙烯酸酯聚合物其各组分的质量份数为:丙烯酸异辛酯60份醋酸乙烯酯30份丙烯酸羟乙酯8份丙烯酸缩水甘油...
【专利技术属性】
技术研发人员:庄蒙晰,
申请(专利权)人:上海巍盛化工科技有限公司,
类型:发明
国别省市:上海,31