The invention discloses a new cable material, whose raw materials include epoxy resin 100 120, polyvinyl ethylene 10 30, carbon fiber 20 50, glass fiber 1 3, EPDM 20 30, Microencapsulated Red Phosphorus 10 20, flame retardant chemical fiber 5 10, CPE flame retardant 1 2, zinc oxide 0.1 0.3, stearic acid 0.4, CPE flame retardant. In the preparation of epoxy resin, phenolic resin was dissolved in ethanol, silane coupling agent was added to modify carbon nanotubes, stirring, rotating evaporation was added to remove ethanol, and material A was dried. Material A and EPDM were mixed, heated and stirred to obtain epoxy resin. The invention has good thermal conductivity and high mechanical performance.
【技术实现步骤摘要】
一种新型电缆材料
本专利技术涉及电缆材料
，尤其涉及一种新型电缆材料。
技术介绍
三元乙丙橡胶具有良好的耐热性、耐腐蚀性、绝缘性和机械性能，可广泛用于汽车部件、建筑用防水材料、电线电缆护套、耐热胶管、胶带、汽车密封件、电子电气等领域，但是三元乙丙橡胶的导热率很低，是热的不良导体，从而限制了三元乙丙橡胶的应用。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种新型电缆材料，本专利技术耐热导热性好，机械性能高，耐腐蚀性好。本专利技术提出的一种新型电缆材料，其原料按重量份包括：环氧树脂100-120份，聚偏二幅乙烯10-30份，碳纤维20-50份，玻璃纤维1-3份，三元乙丙橡胶20-30份，微胶囊化红磷10-20份，阻燃化学纤维5-10份，CPE阻燃剂1-2份，氧化锌0.1-0.3份，硬脂酸0.2-0.4份，CPE阻燃剂M0.2-0.4份，Ca/Zn复合稳定剂4-6份，蒙旦蜡2-4份；其中，在环氧树脂的制备过程中，将酚醛树脂加入乙醇中溶解，加入硅烷偶联剂改性碳纳米管，搅拌，旋转蒸发除去乙醇，干燥得到物料A；将物料A和三元乙丙橡胶混匀，升温，保温搅拌得到环...
【技术保护点】
1.一种新型电缆材料，其特征在于，其原料按重量份包括：环氧树脂100‑120份，聚偏二幅乙烯10‑30份，碳纤维20‑50份，玻璃纤维1‑3份，三元乙丙橡胶20‑30份，微胶囊化红磷10‑20份，阻燃化学纤维5‑10份，CPE阻燃剂1‑2份，氧化锌0.1‑0.3份，硬脂酸0.2‑0.4份，CPE阻燃剂M0.2‑0.4份，Ca/Zn复合稳定剂4‑6份，蒙旦蜡2‑4份；其中，在环氧树脂的制备过程中，将酚醛树脂加入乙醇中溶解，加入硅烷偶联剂改性碳纳米管，搅拌，旋转蒸发除去乙醇，干燥得到物料A；将物料A和三元乙丙橡胶混匀，升温，保温搅拌得到环氧树脂。
【技术特征摘要】
1.一种新型电缆材料，其特征在于，其原料按重量份包括：环氧树脂100-120份，聚偏二幅乙烯10-30份，碳纤维20-50份，玻璃纤维1-3份，三元乙丙橡胶20-30份，微胶囊化红磷10-20份，阻燃化学纤维5-10份，CPE阻燃剂1-2份，氧化锌0.1-0.3份，硬脂酸0...