The invention discloses a production process of silicon carbide extrusion molding, which belongs to the technical field of silicon carbide processing. It includes the following steps: (1) Silicon carbide powder A with D50 value of 35 40 um and SiC powder B with D50 value of 5.5 6.0 um are fully mixed for 10 minutes to obtain SiC mixed powder; (2) slurry aging 24 hours after ball milling; (3) extrusion moulding; (4) shade-dried tube blank; (5) drying; (6) high temperature sintering of SiC pipe. The silicon carbide extrusion forming process of the invention has the advantages of high yield of extrusion products, effective reduction of blank breakage rate of products, high strength of finished products and 90% qualified rate of sintered products.
【技术实现步骤摘要】
一种碳化硅挤出成型生产工艺
本专利技术涉及一种碳化硅挤出成型生产工艺，属于碳化硅加工
技术介绍
碳化硅陶瓷具有高硬度、高分解温度、高导热率、低膨胀、耐腐蚀等多种优良特性，已在机械、石油、汽车工业等领域大显身手。随着现代国防、空间技术以及能源技术的迅速发展，碳化硅作为高技术陶瓷，特别是高性能结构陶瓷的应用日益广泛，如作为高温热机材料诸如高温燃汽轮机的燃烧室、涡轮机叶片、涡轮增压器转子、高温喷嘴等的主要候选材料。与此同时，对碳化硅陶瓷几何形状的复杂性、韧性、强度及可靠性的要求越来越高。碳化硅的结构特点决定了它的一系列优良性能，高强度、高硬度、耐高温、抗氧化、高热导率、低热膨胀率、具有优良的化学稳定性以及不被大多数的酸碱溶液所腐蚀。碳化硅陶瓷材料还具有高温抗氧化特性。高温氧化时表面生成致密的保护膜，抑制了氧的进一步氧化,因此具有优异的抗氧化性能。碳化硅陶瓷所具备的优良性能使其在机械、化工、能源、军工等使用环境苛刻的应用领域中展示着重要的应用前景。
技术实现思路
本专利技术的目的在于提供了一种碳化硅挤出成型生产工艺，该工艺制得的坯体强度较高,脱模或者干燥过程中不易开...
【技术保护点】
1.一种碳化硅挤出成型生产工艺，其特征在于，包括以下步骤：（1）、将D50值为35‑40μm的碳化硅微粉A和D50值为5.5‑6.0μm的碳化硅微粉B充分混合10分钟，得碳化硅混合微粉；（2）、球磨：按照一定的比例称取碳化硅混合微粉、分散剂、烧结助剂和去离子水,滴加氨水调节其值至10.5,按照球料比为3:1取玛瑙磨球,放入球磨罐中,将球磨罐放在轻型罐磨机上球磨20小时；然后浆料陈腐24小时；（3）、挤出成型：将碳化硅料浆放入挤出机内进行挤出成型，得管材素坯；（4）、阴干定型管材素坯：将管材素坯转移到阴干定型工具上，管材素坯于室内阴干2天；（5）烘干：将从管材素坯放入恒温干燥...
【技术特征摘要】
1.一种碳化硅挤出成型生产工艺，其特征在于，包括以下步骤：（1）、将D50值为35-40μm的碳化硅微粉A和D50值为5.5-6.0μm的碳化硅微粉B充分混合10分钟，得碳化硅混合微粉；（2）、球磨：按照一定的比例称取碳化硅混合微粉、分散剂、烧结助剂和去离子水,滴加氨水调节其值至10.5,按照球料比为3:1取玛瑙磨球,放入球磨罐中,将球磨罐放在轻型罐磨机上球磨20小时；然后浆料陈腐24小时；（3）、挤出成型：将碳化硅料浆放入挤出机内进行挤出成型，得管材素坯；（4）、阴干定型管材素坯：将管材素坯转移到...
【专利技术属性】
技术研发人员：龚志刚，闫帅帅，郝文虎，马坤，毕见强，韩宇，龚洋，张霞，徐勤龙，高志民，马丽，
申请(专利权)人：山田研磨材料有限公司，
类型：发明
国别省市：山东,37