The invention discloses an acrylate pressure sensitive adhesive, which comprises the following raw materials: 690-844 parts of butyl acrylate; 3.450-4.230 parts of acrylic acid; 0.089-0.109 parts of initiator; 0.780-0.960 parts of emulsifier; 0.344-0.420 parts of buffer; 0.070-0.086 parts of carved white block; and 533.81-652.43 parts of water. The above-mentioned acrylate pressure-sensitive adhesive, pressure-sensitive adhesive tape and its preparation method have simple raw material formula, no need to use tackifier, softener, antioxidant and other additives, less toxicity of raw materials, less pollutants generated in the preparation process, and the pollutants generated are collected and treated, further reducing the environmental impact.
【技术实现步骤摘要】
丙烯酸酯压敏胶黏剂、压敏胶带及其制备方法
本专利技术属于压敏胶
，具体涉及一种丙烯酸酯压敏胶黏剂、压敏胶带及其制备方法。
技术介绍
压敏胶带是一种特殊类型的胶带，将一种压敏胶黏剂涂于带状基材上制成的。压敏胶黏剂是压敏胶带最重要的组成部分，其作用是使胶带具有对压力敏感的粘附力。丙烯酸酯类压敏胶是工业上使用最多的压敏胶类型之一，由于其分子结构中不含有不饱和键而具有耐老化、耐光、粘接面广、无色透明的优点，但是其在制备过程中毒性较高，对环境的影响较大。现有胶带制备中使用基材不可降解，会造成严重的环境污染。
技术实现思路
本专利技术针对传统的丙烯酸酯压敏胶制备过程中毒性较高，对环境影响大的问题，提供一种丙烯酸酯压敏胶黏剂、压敏胶带及其制备方法。本专利技术提供的一种丙烯酸酯压敏胶黏剂，所述丙烯酸酯压敏胶黏剂包括以下重量份数的原料：丙烯酸丁酯690～844份；丙烯酸3.450～4.230份；引发剂0.089～0.109份；乳化剂0.780～0.960份；缓冲剂0.344～0.420份；雕白块0.070～0.086份；以及水533.81～652.43份。在其中一个实施例中，所述...
【技术保护点】
1.一种丙烯酸酯压敏胶黏剂，其特征在于，所述丙烯酸酯压敏胶黏剂包括以下重量份数的原料：丙烯酸丁酯 690～844份；丙烯酸 3.450～4.230份；引发剂 0.089～0.109份；乳化剂 0.780～0.960份；缓冲剂 0.344～0.420份；雕白块 0.070～0.086份；以及水 533.81～652.43份。
【技术特征摘要】
1.一种丙烯酸酯压敏胶黏剂，其特征在于，所述丙烯酸酯压敏胶黏剂包括以下重量份数的原料：丙烯酸丁酯690～844份；丙烯酸3.450～4.230份；引发剂0.089～0.109份；乳化剂0.780～0.960份；缓冲剂0.344～0.420份；雕白块0.070～0.086份；以及水533.81～652.43份。2.根据权利要求1所述的丙烯酸酯压敏胶黏剂，其特征在于，所述丙烯酸酯压敏胶黏剂由包括以下重量份数的原料制备而成：丙烯酸丁酯767份；丙烯酸3.840份；引发剂0.099份；乳化剂0.870份；缓冲剂0.382份；雕白块0.078份；以及水593.12份。3.根据权利要求1所述的丙烯酸酯压敏胶黏剂，其特征在于，所述引发剂为过硫酸铵。4.根据权利要求1所述的丙烯酸酯压敏胶黏剂，其特征在于，所述乳化剂为联苯醚磺酸盐。5.根据权利要求1所述的丙烯酸酯压敏胶黏剂，其特征在于，所述缓冲剂为2,6-二叔丁基对甲酚。6.根据权利要求1至5任意一项所述的丙烯酸酯压敏胶黏剂，其特征在于，所述丙烯酸酯胶...
【专利技术属性】
技术研发人员：严国标，王洪军，汪兴华，应龙，章海林，
申请(专利权)人：绍兴明基新材料有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。