A processing method of ceramic wear-resistant glaze is introduced. According to the weight fraction, 40-50 quartz, 20-25 kaolin, 5-8 feldspar powder, 3-5 corundum and 2-5 talc powder are mixed, 8-10 zircon, 2-3 limestone and 0.8-1.0 borax are added to obtain dry material, and then 20-30% water is added to the total quality of dry material. After ball milling and grinding, the remaining 0.08%-0.10% of the 250 mesh sieve was obtained, and the ceramic wear-resistant glaze was obtained by drying. The advantages are: simple process, reasonable proportioning, spinel structure formed by alumina in corundum and kaolin, melting property of glaze can be adjusted by increasing the content of free corundum in structure to ensure glaze quality, firing ceramics, good mechanical strength, high glaze hardness and good thermal stability.
【技术实现步骤摘要】
一种陶瓷耐磨釉料的加工方法
本专利技术涉及一种陶瓷耐磨釉料的加工方法。
技术介绍
瓷器是人们日常生活中必不可少的生活用品，日常使用的餐具一般都是普通日用陶瓷制品，日用瓷器具有以下优点：1.易于洗涤和保持清洁；2.热稳定性好、传热慢；3.化学性质稳定，经久耐用；4.瓷器的气孔极少，吸水率低；5.彩釉装饰丰富多彩，尤其是高温无铅釉彩，很受人们欢迎。随着瓷器的发展，不单对美观度的要求提高，对釉料的强度要要求也不短提高，陶瓷的釉面强度必须竖硬，现有的釉料的强度和硬度都远远达不到要求，使用寿命较短。
技术实现思路
本专利技术要解决的技术问题是提供一种陶瓷耐磨釉料的加工方法，该釉料在陶瓷彩烧时使用，制作的陶瓷釉面，美观，强度高，耐磨性好，具有装饰瓷器表面的作用。本专利技术的技术解决方案是：一种陶瓷耐磨釉料的加工方法，其具体步骤如下：按重量份数计，选取的40份～50份石英、20份～25份高岭土、5份～8份长石粉、3份～5份刚玉和2份～5份滑石粉混合，加入8份～10份锆英石、2份～3份石灰石和0.8份～1.0份硼砂，得到干物料，然后加入占干物料总质量20％～30％的水，经过球磨粉碎后，得到过250目筛筛余0.08％～0.10％，烘干，得到陶瓷耐磨釉料。本专利技术的有益效果：工艺简单，配料合理，刚玉与高岭土中的氧化铝形成尖晶石结构，通过加大结构内游离刚玉的含量调整釉料熔融性能，高岭土具有遮盖性，提高釉料白度和透明度，然后通过合理的烧成温度，快速釉烧，确保釉面质量，烧成陶瓷，机械强度好，釉面硬度高，热稳定性好，并具有良好的白度和透明度高。具体实施方式实施例1选取的40kg石英、2...
【技术保护点】
1.一种陶瓷耐磨釉料的加工方法，其特征是：具体步骤如下：按重量份数计，选取的40份～50份石英、20份～25份高岭土、5份～8份长石粉、3份～5份刚玉和2份～5份滑石粉混合，加入8份～10份锆英石、2份～3份石灰石和0.8份～1.0份硼砂，得到干物料，然后加入占干物料总质量20％～30％的水，经过球磨粉碎后，得到过250目筛筛余0.08％～0.10％，烘干，得到陶瓷耐磨釉料。
【技术特征摘要】
1.一种陶瓷耐磨釉料的加工方法，其特征是：具体步骤如下：按重量份数计，选取的40份～50份石英、20份～25份高岭土、5份～8份长石粉、3份～5份刚玉和2份～5份滑石粉混合，加入8份～10...
【专利技术属性】
技术研发人员：刘福，王立明，
申请(专利权)人：喀左御成紫陶制品有限公司，
类型：发明
国别省市：辽宁,21