The invention relates to a preparation method of raw materials for chemical fiber production, which belongs to the technical field of textile production. Material selection: choose protein powder fiber for fine grinding, fine grind into 2 to 3mm particle size, mix protein powder particles with fibrous raw materials, add deionized water, dilute the concentration of 0.15 to 2.5, get the slurry, mix the dispersant three ethyl hexyl phosphoric acid with water 1:3, add the slurry to 30 to 50 minutes at high temperature 100 to 200 degrees, and form emulsion. At room temperature, stir the cold emulsion and put it into a vacuum processor for 5 to 6 hours to get the raw material. The method has simple preparation process, high mechanical strength and stability. The main raw material is pure natural protein fibers, which can ensure the air permeability and moisture absorption properties of the fibers.
【技术实现步骤摘要】
一种化学纤维生产原料的制备方法
本专利技术涉及一种化学纤维生产原料的制备方法，属于纺织品生产
技术介绍
化学纤维广泛应用在纺织品生产中。化学纤维决定纺织品面料的特性，常用的化学纤维通常选用有机成分，如聚丙烯腈，这类有机成分具有很好的染色性能及光泽手感，但是只有染色效果好，易上色，颜料中的颗粒分散体不稳定，容易出现染色不均匀的现象；而且现有的其他有机成分制成的纤维如人造纤维，其吸收性能和透气性能、抗电性能均达不到要求。
技术实现思路
本专利技术是为了弥补上述技术存在的缺陷，提供了一种化学纤维生产原料的制备方法，该方法制备工艺简单，具有较高的力学强度和稳定性，原料主体采用纯天然蛋白纤维，能够保证纤维的透气、吸湿性能，同时，添加悬浊分散剂使原料中分散体稳定，使得颜料均匀附着于衣料内层及表面，符合纤维染色标准。为了实现上述目的，本专利技术所采用的技术方案为：一种化学纤维生产原料的制备方法，具体步骤如下：材料选取：选用蛋白粉纤维进行细磨，细磨成粒径为2—3mm的颗粒；将蛋白粉颗粒与纤维原料混合，加入去离子水，稀释，稀释浓度为0.15—2.5，得到浆液。将分散剂三乙基己...
【技术保护点】
1.一种化学纤维生产原料的制备方法，具体步骤如下：材料选取：选用蛋白粉纤维进行细磨，细磨成粒径为2—3mm的颗粒；将蛋白粉颗粒与纤维原料混合，加入去离子水，稀释，稀释浓度为0.15—2.5，得到浆液；将分散剂三乙基己基磷酸与水的比例为1：3混匀，加入浆液在100—200度下高温分散30—50分钟，形成乳液，冷却至常温；将冷去后的乳液搅拌，放入真空处理器中脱泡5—6小时，得到原料。
【技术特征摘要】
1.一种化学纤维生产原料的制备方法，具体步骤如下：材料选取：选用蛋白粉纤维进行细磨，细磨成粒径为2—3mm的颗粒；将蛋白粉颗粒与纤维原料混合，加入去离子水，稀释，稀释浓度为0.15—2.5，...
【专利技术属性】
技术研发人员：宋丛恺，
申请(专利权)人：青岛凯玉盈商贸有限公司，
类型：发明
国别省市：山东,37