The invention relates to a cast iron cutting fluid and a preparation method thereof. The invention belongs to the field of chemical technology and relates to a cutting fluid, which comprises 80 86 portions of boric acid, 160 172 portions of ethylene glycol, 280 310 portions of vegetable oleic acid, 30 40 portions of OP 10 emulsifier, 10 15 portions of defoamer, 400 450 portions of triethanolamine, and 10 15 portions of DF 53 surfactant. The cutting fluid of the invention has excellent lubricity, rust-proof, cooling and cleaning properties, can effectively reduce friction force in metal processing, reduce friction heat, and ensure the smoothness of the workpiece processed without any harm to human body, and is green and environmental. Moreover, the invention adopts non-toxic and non-irritating odor additives, which do not damage human skin, is convenient to use and safe to operate, does not cause harmful effects such as air bubbles, cracking and falling off of machine tool paint, and has good storage stability and long service life.
【技术实现步骤摘要】
一种铸铁切削液及其制备方法
专利技术属于化工
，涉及一种铸铁切削液及其制备方法。
技术介绍
金属切削加工是金属加工中最常见、应用最广泛的一种。切削液是金属切削加工的重要的配套材料。使用金属切削液的目的就是降低切削力及刀具与工件之间的摩擦，及时带走切削区内产生的热量以降低切削温度，减少刀具磨损，提高刀具耐用度，从而提高生产效率，改善工件表面粗糙度，保证工件加工精度，达到最佳经济效果。因此，使用切削液是提高加工质量和降低加工成本的重要措施。随着切削技术的不断发展，对切削液性能要求也越来越高。
技术实现思路
本专利技术的目的在于：提供一种性能优越的切削液及其制备方法。为了实现上述专利技术目的，本专利技术提供如下技术方案：一种切削液，包括以下重量份的原料：硼酸80-86份，乙二醇160-172份，植物油酸280-310份，OP-10乳化剂30-40份，消泡剂10-15份，三乙醇胺400-450份，DF-53表面活性剂10-15份。优选地，所述的切削液，包括以下重量份的原料：硼酸82份，乙二醇165份，植物油酸300份，OP-10乳化剂35份，消泡剂12份，三乙醇胺420...
【技术保护点】
1.一种切削液，其特征在于，包括以下重量份的原料：硼酸80‑86 份，乙二醇160‑172份，植物油酸280‑310份，OP‑10乳化剂30‑40 份，消泡剂10‑15份，三乙醇胺400‑450份，DF‑53表面活性剂10‑15 份。
【技术特征摘要】
1.一种切削液，其特征在于，包括以下重量份的原料：硼酸80-86份，乙二醇160-172份，植物油酸280-310...