一种防锈润滑剂制造技术

本发明专利技术涉及一种润滑剂，具体是一种防锈润滑剂，由以下质量份的组分组成：复配成膜剂1‑5％、金属纳米粉1‑5％、植物油85‑95％、防锈剂1‑2％、抗磨防蚀剂1‑5％；所述金属纳米粉选自：纳米铜、纳米镍、纳米铋、纳米钼中的一种；所述植物油选自：菜籽油、葵花籽油、花生油、大豆油、蓖麻油、橄榄油、玉米油中的至少一种。采用本发明专利技术的防锈润滑剂，更环保，生物降解率高，抗磨减摩能力好，提高摩擦副承载能力，延长设备的使用寿命。

A rust-proof lubricant

The invention relates to a lubricant, in particular to a rust-proof lubricant, which is composed of the following components: compound film-forming agent 1 5%, metal nanopowder 1 5%, vegetable oil 85 95%, rust-proof agent 1 2%, anti-abrasion and anti-corrosion agent 1 5%; the metal nanopowder is selected from one of nano-copper, nano-nickel, Nano-Bismuth and nano-molybdenum; the vegetable oil is selected from rapeseed oil, Nano-Bismuth and nano-molybdenum At least one of sunflower seed oil, peanut oil, soybean oil, castor oil, olive oil and corn oil. The anti-rust lubricant of the invention is more environmentally friendly, has high biodegradability, good anti-wear and friction reduction ability, improves the bearing capacity of friction pairs, and prolongs the service life of the equipment.

【技术实现步骤摘要】
一种防锈润滑剂
本专利技术涉及一种润滑剂，具体是一种防锈润滑剂。
技术介绍
金属锈蚀是自然界的一个自发趋势，钢铁产品防锈方法通常是涂防锈油。涂油不仅带来产品和环境的污染，还会给钢材深加工企业带来一系列麻烦。防锈润滑剂具有优异的防止生锈、降低摩擦系数性能，在民用和工业生产上使用相当广泛。随着防锈润滑剂的广泛使用，防锈润滑剂可通过多种途径进入环境中，给生态环境造成污染。现有的防锈润滑剂和防锈润滑矿物油的生物降解性能差、生态毒性积累性强，严重污染陆地、江河和湖泊，危害生态环境和生态平衡，对环境造成恶劣影响。现有防锈润滑剂技术中，主要是通过向防锈润滑剂中加入各种功能性助剂，对防锈润滑剂进行改性，以改善防锈介质的理化性能，提高润滑能力并降低摩擦系数等。这类功能性助剂虽能在一定程度上起到改善摩擦作用，但在使用中摩擦面的摩擦损伤和生锈腐蚀无法解决。
技术实现思路
本专利技术的目的是克服现有技术中防锈润滑剂生物降解性能差、生态毒性积累性强的技术不足，提供一种既环保又能减少表面摩擦损伤和生锈腐蚀的防锈润滑剂。为了解决上述技术问题，本专利技术采用的技术方案如下：一种防锈润滑剂，由以下质量份的组分组成：复配成本文档来自技高网...

【技术保护点】
1.一种防锈润滑剂，其特征在于由以下质量份的组分组成：复配成膜剂1‑5％、金属纳米粉1‑5％、植物油85‑95％、防锈剂1‑2％、抗磨防蚀剂1‑5％。

【技术特征摘要】
1.一种防锈润滑剂，其特征在于由以下质量份的组分组成：复配成膜剂1-5％、金属纳米粉1-5％、植物油85-95％、防锈剂1-2％、抗磨防蚀剂1-5％。2.根据权利要求1所述的一种防锈润滑剂，其特征在于所述金属纳米粉选自：纳米铜、纳米镍、纳米铋、纳米钼中的一种。3.根据权利要求1所述的一种防锈润滑剂，其特征在于所述植物油选自：菜籽油、...

【专利技术属性】
技术研发人员：魏倩，
申请(专利权)人：丹阳市宁大卫防检测技术有限公司，
类型：发明