The invention provides a preparation method of lithium ion battery. The electrolyte of the lithium ion battery includes ethylene sulfate and sodium hexafluorophosphate as additives, in which ethylene sulfate accounts for 0.5_3% of the total volume of the electrolyte, and the concentration of sodium hexafluorophosphate in the electrolyte is 0.001_0.02mol/L. The conversion method includes the formation in the atmosphere of high concentration carbon dioxide. The first step and the second step formed in the atmosphere of low or zero concentration carbon dioxide can form a stable SEI film by the method of the present invention, avoid the increase of internal resistance and reduce the volume expansion rate of the battery after circulation, especially at high temperature.
【技术实现步骤摘要】
一种锂离子电池的制备方法
本专利技术涉及软包装锂离子电池
，特别是涉及一种锂离子电池的制备方法。
技术介绍
新能源汽车新政策释放了推动电池性能提升、增大能量密度的信号。随着补贴门槛的不断提升，锂离子电池作为一种电池轻量化高能化的手段，以较高比例占据市场。锂离子电池能够助力更多电池企业提升能量密度和产品竞争力。硫酸亚乙酯作为锂离子电池电解液常用的添加剂，其作用在于抑制电池初始容量的下降，增大初始放电容量，减少高温放置后的电池膨胀，提高电池的充放电性能及循环次数，但是硫酸亚乙酯的加入会导致电池内阻的增加，从而影响电池的倍率性能，进一步的，专利技术人发现，在含有二氧化碳的气氛下化成，能够进一步降低内阻，但是随着循环次数的增加，电池的体积依然会发生较大程度的膨胀，因此需要提供一种提高电池的充放电性能及循环次数的方法。
技术实现思路
本专利技术提供了一种锂离子电池的制备方法，所述锂离子电池的电解液中包括硫酸亚乙酯以及六氟磷酸钠作为添加剂，其中，硫酸亚乙酯占电解液总体积的0.5-3％，六氟磷酸钠在电解液中的浓度为0.001-0.02mol/L，其中所述化成方法包括在高浓度二...
【技术保护点】
1.一种锂离子电池的制备方法，所述锂离子电池的电解液中包括硫酸亚乙酯以及六氟磷酸钠作为添加剂，其中，硫酸亚乙酯占电解液总体积的0.5‑3％，六氟磷酸钠在电解液中的浓度为0.001‑0.02mol/L，其中所述化成方法包括在高浓度二氧化碳的气氛下化成的第一步骤，以及在低浓度或0浓度二氧化碳的气氛下化成的第二步骤。
【技术特征摘要】
1.一种锂离子电池的制备方法，所述锂离子电池的电解液中包括硫酸亚乙酯以及六氟磷酸钠作为添加剂，其中，硫酸亚乙酯占电解液总体积的0.5-3％，六氟磷酸钠在电解液中的浓度为0.001-0.02mol/L，其中所述化成方法包括在高浓度二氧化碳的气氛下化成的第一步骤，以及在低浓度或0浓度二氧化碳的气氛下化成的第二步骤。2.如权利要求1所述的方法，其中步骤包括：1)、注入电解液，所述电解液中包括硫酸亚乙酯以及六氟磷酸钠作为添加剂，其中，硫酸亚乙酯占电解液总体积的0.5-3％，六氟磷酸钠在电解液中的浓度为0.001-0.02mol/L；2)、将注液后的锂离子电池移入密封装置中进行恒流充电至预定电压，其中所述密封装置中的气氛为含有体积百分比10％以上的二氧化碳的惰性气体；3)、以所述预定电压恒压充电，直至充电电流降至预定值以下；4)、在所述预定电压附近进行恒流充放电循环若干次；5...