The present invention relates to a method for clarifying alkali-free glass by vacuum melting, including the ingredients of existing alkali-free glass batches, heating melting, clarifying, iron plate casting, annealing, cutting and polishing processes; and its characteristics are as follows: before heating melting, the melting furnace is decompressed to control the vacuum in the furnace at 500 Pa 100 000 Pa, using 0.5 1 hour; after clarification, melting to the furnace. Air is introduced into the furnace to adjust the pressure balance inside and outside the furnace. The advantages of the present invention are: vacuum melting and vacuum clarification of batches to achieve uniformity and completeness of reaction between batches, to achieve the best melting, clarification and homogenization effect, and to obtain high quality alkali-free glass with less residual bubbles, small bubble diameter and good homogeneity.
【技术实现步骤摘要】
一种无碱玻璃减压熔制澄清方法
本专利技术属无碱玻璃制备领域，涉及一种无碱玻璃减压熔制澄清方法。
技术介绍
液晶显示装置等显示器用的玻璃基板被要求实质上不含碱金属，由于无碱玻璃的玻璃原料中实质上不含碱金属化合物，且氧化铝含量高，导致玻璃熔制、澄清过程比常规钠钙硅酸盐玻璃难度大很多，普通的常压熔制、澄清得到的玻璃样品气泡较多。玻璃熔制过程中，气泡是一种最为常见的缺陷，它会影响玻璃制品的外观、透过率、机械强度和硬度等，当无碱玻璃基板残存有一定数量微气泡且均质性不好时，进而无法满足液晶显示装置等显示器用的玻璃基板要求。
技术实现思路
本专利技术的目的是为了解决无碱玻璃熔制、澄清过程中气泡多，影响玻璃品质的问题，提供一种无碱玻璃减压熔制澄清方法。为了实现上述目的，本专利技术采用的技术方案如下：一种无碱玻璃减压熔制澄清方法，包括现有无碱玻璃配合料的配料、升温熔制、澄清、铁板浇铸成型、退火、切割与抛光工序；其特征在于：在升温熔制之前，先将熔化炉进行减压处理，控制炉内真空度在500Pa-100000Pa，用时0.5-1小时；澄清结束后向熔化炉中通入空气，调节炉内外气压平衡。进一步，所...
【技术保护点】
1.一种无碱玻璃减压熔制澄清方法，包括现有无碱玻璃配合料的配料、升温熔制、澄清、铁板浇铸成型、退火、切割与抛光工序；其特征在于：在升温熔制之前，先将熔化炉进行减压处理，控制炉内真空度在500Pa‑100000Pa，用时0.5‑1小时；澄清结束后向熔化炉中通入空气，调节炉内外气压平衡。
【技术特征摘要】
1.一种无碱玻璃减压熔制澄清方法，包括现有无碱玻璃配合料的配料、升温熔制、澄清、铁板浇铸成型、退火、切割与抛光工序；其特征在于：在升温熔制之前，先将熔化炉进行减压处理，控制炉内真空度在500Pa-100000Pa，用时0.5-1小时；澄清结束后向熔化炉中通入空气，调节炉内外气压平衡。2.根据权利要求1所述一种无碱玻璃减压熔制澄清方法，其特征在于：所述无碱玻璃的配合料由以下重量百分比的原料组成：57-66%的SiO2、14-18%的Al2O3、0.5-1%的ZrO2、6-11%的B2O3、3-6%的MgO、2-4%...