The invention relates to a method for preparing denitrification catalyst by selective catalytic reduction technology, in particular to a catalyst cleaning process for efficient removal of black and arsenic with pH neutral cleaning solution. The aim of the present invention is to provide a regeneration method of a catalyst for denitrification by selective catalytic reduction technology of black arsenic poisoning. Under the condition of neutral acidity and basicity, the black arsenic on the surface of the catalysts for selective catalytic reduction can be removed to the greatest extent, and the original mechanical strength of the catalysts can not be reduced. The loss of active components of the catalysts for selective catalytic reduction can be reduced as much as possible after cleaning. A certain anti-poisoning additive is implanted to make the catalysts have certain anti-black arsenic poisoning ability.
【技术实现步骤摘要】
一种选择性催化还原技术制备脱硝催化剂的方法
专利技术涉及一种选择性催化还原技术制备脱硝催化剂的方法。
技术介绍
选择性催化还原技术脱硝技术对锅炉烟气NOx控制效果显著、技术成熟，已成为世界上应用最多、最有成效的烟气脱硝技术之一。近年来.我国选择性催化还原技术脱硝工程发展迅速，在燃煤电厂的应用也更为普及，脱硝催化剂的市场装载量也逐年增长。但由于催化剂的化学寿命通常为16000～24000h，随之带来了较大的失活催化剂处置压力，目前国内已经出现失活选择性催化还原技术脱硝催化剂的更换需求并即将迎来高峰期。现有商用钒钛系脱硝催化剂随意堆存或不当处置，将造成二次污染和资源浪费。加之一般催化剂的机械寿命是化学寿命的2-3倍，且再生后的催化剂活性可恢复至新鲜催化剂的90％甚至100％以上，接近新鲜催化剂水平，价格却是新鲜催化剂的一半甚至更低，所以再生被视为催化剂更换最为经济和环保的方式。黑砷中毒是引起催化剂失活的常见原因之一，主要是由烟气中的气态黑黑砷2O3引起：(1)气态黑黑砷2O3分子进入催化剂微孔，并固化在活性、非活性区域，形成黑砷的饱和层，加之黑黑砷盐在催化剂微孔内的堵...
【技术保护点】
1.一种选择性催化还原技术制备脱硝催化剂的方法，其特征在于：包括以下步骤：步骤一：物理净化，通过物理方式对催化剂进行清理，清除催化剂表面的积灰和孔道的疏通；步骤二：离子水清洗，对催化剂进行去离子水清洗，然后进行加热干燥；步骤三：活性浸渍，将步骤二获得的催化剂浸渍在再生液中，浸渍时间为20‑60分钟；步骤四：活化激活，对步骤三获得的催化剂进行高温活化激活，活化激活的温度在350‑500℃之间，活化时间为2‑6小时。
【技术特征摘要】
1.一种选择性催化还原技术制备脱硝催化剂的方法，其特征在于：包括以下步骤：步骤一：物理净化，通过物理方式对催化剂进行清理，清除催化剂表面的积灰和孔道的疏通；步骤二：离子水清洗，对催化剂进行去离子水清洗，然后进行加热干燥；步骤三：活性浸渍，将步骤二获得的催化剂浸渍在再生液中，浸渍时间为20-60分钟；步骤四：活化激活，对步骤三获得的催化剂进行高温活化激活，活化激活的...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。