The invention discloses a heat-resistant iron-based alloy and its preparation method, which mainly relates to the technical field of alloy materials, including Fe, Ti, Ni, Ba, Cd and Si. The mass fraction of Ti is 0.3 0.7%, the mass fraction of Ni is 3.5 5%, the mass fraction of Ba is 0.08 0.15%, the mass fraction of Cd is 0.4 0.7%, the mass fraction of Si is 2.3 3.7%, and the remainder of Fe and Ni is the guaranteed shape. Adequate austenite is formed, high temperature resistance is improved, Ba is added to improve high temperature heat strength for melting strengthening. At the same time, Cd can form part of carbide to improve hardness, enhance wear resistance, reduce the cost of alloy powder manufacturing by more than 1/3, improve efficiency and save cost.
【技术实现步骤摘要】
一种耐热铁基合金及其制备方法
本专利技术主要涉及合金材料
，具体是一种耐热铁基合金及其制备方法。
技术介绍
高温耐磨机械零部件国内外常用的有钴基(如stellite6#)和镍基(如Ni50、Ni45)高温耐磨合金，但由于我国CO、Ni原料资源缺乏，价格昂贵，因此国内市场渴望研发一种具有CO、Ni基合金粉末性能，同时价格低廉的替代合金粉末，铁基合金粉末材料相对于传统的耐磨材料来说，具有良好的韧性、塑性，可以做为耐磨材料的首选。但目前常用的铁基合金粉末一般由B、Si、W、Ni、Cr等元素组成，其高温耐磨性、耐腐蚀性、抗氧化性均与钴基(如stellite6#)和镍基(如Ni50)高温耐磨合金有一定差距，不能满足人们的实际需求。
技术实现思路
鉴于现有技术中存在的不足和缺陷，本专利技术提供了一种耐热铁基合金及其制备方法及其制备方法。为了解决上述技术问题，本专利技术采用如下技术方案：一种耐热铁基合金及其制备方法，包括Fe、Ti、Ni、Ba、Cd、Si，所述Ti的质量分数为0.3-0.7％、Ni的质量分数为3.5-5％、Ba的质量分数为0.08.-0.15.％、Cd的质量分...
【技术保护点】
1.一种耐热铁基合金，其特征在于：包括Fe、Ti、Ni、Ba、Cd、Si，所述Ti的质量分数为0.3‑0.7％、Ni的质量分数为3.5‑5％、Ba的质量分数为0.08.‑0.15.％、Cd的质量分数为0.4‑0.7％、Si的质量分数为2.3‑3.7％，余量为Fe。
【技术特征摘要】
1.一种耐热铁基合金，其特征在于：包括Fe、Ti、Ni、Ba、Cd、Si，所述Ti的质量分数为0.3-0.7％、Ni的质量分数为3.5-5％、Ba的质量分数为0.08.-0.15.％、Cd的质量分数为0.4-0.7％、Si的质量分数为2.3-3.7％，余量为Fe。2.根据权利要求1所述的一种耐热铁基合金，其特征在于：所述Ti的质量分数为0.3-％、Ni的质量分数为3.5％、Ba的质量分数为0.08.％、Cd的质量分数为0.4％、Si的质量分数为2.3％，余量为Fe。3.根据权利要求1所述的一种耐热铁基合金，其特征在于：所述Ti的质量分数为0.7％、Ni的质量分数为5％、Ba的质量分数为0.15％、Cd的质量分数为0.7％、Si的质量分数为3.7％，余量为Fe。4.根据权利要求1所述的一种耐热铁基合金，其特征在于：所述Ti的质量分数为0.45％、Ni的质量分数为4％、Ba的质量分数为0.1％、Cd的质量分数为0.5％、Si的质量分数为2.7％，余量为Fe。5.根据权利要求1所述的一种...