The invention discloses an adhesive for the construction of early high strength and fast tunnel anchor bolt and cable, which consists of 100-120 portions of sulphoaluminate cement or 80-100 Portland cement, 12-15 portions of water reducing agent, 3-5 portions of accelerator, 8-10 portions of expansion agent, 2-3 portions of thickener, and 1-2 portions of crystal silicon cutting mortar. The adhesives used in the construction of early high strength and fast tunnel anchor rope can solidify quickly in a short time, so that the tension strength meets the design requirements, achieves good results, ensures the close connection of construction procedures, and saves a lot of construction time and cost.
【技术实现步骤摘要】
早高强快速隧道锚杆锚索施工用粘合剂
本专利技术涉及锚固的
，尤其涉及一种注浆锚固材料。
技术介绍
锚杆锚索是隧道、桥梁、地下车站等地下工程施工中加强主动支护的重要方法。在岩锚支护施工过程中，锚索或锚杆的锚固通常采用的做法是先在需要锚固的岩体部位钻孔，然后插入锚索或锚杆，灌注水泥浆或水泥砂浆粘接锚固。但是，传统锚杆锚索进行常规浆材注浆后，由于普通水泥锚固剂硬化时间长，灌浆后需要较长的待凝等强时间，短时间内强度达不到设计张拉强度，影响后续的锚索或锚杆的张拉锁定、支护、开挖等衔接工序，而且易与其它施工工序相互干扰，工期要求紧张的工程往往受到严重的制约，无形中增加施工成本，其根本原因是注浆锚固的材料达不到早强、高强、快速凝结的特点。如中国专利申请号201510662735.5公开的一种锚固砂浆，具体包括以下重量份数的原料：水泥或水泥熟料20～90份；砂子5～70份；早强剂0.01～10份；速凝剂0.01～8份；界面粘结剂0.01～10份；界面渗透剂0.01～10份；微膨胀剂0.01～10份；耐酸粉料0.01～10份；绝缘性能改进剂0.01～10份；缓凝剂0～8份；引...
【技术保护点】
1.一种早高强快速隧道锚杆锚索施工用粘合剂，其特征在于，包括如下重量份的原料：硫铝酸盐水泥100～120份或硅酸盐水泥80～100份、减水剂12～15份、速凝剂3～5份、膨胀剂8～10份、增稠剂2～3份、以及晶体硅切割砂浆1～2份。
【技术特征摘要】
1.一种早高强快速隧道锚杆锚索施工用粘合剂，其特征在于，包括如下重量份的原料：硫铝酸盐水泥100～120份或硅酸盐水泥80～100份、减水剂12～15份、速凝剂3～5份、膨胀剂8～10份、增稠剂2～3份、以及晶体硅切割砂浆1～2份。2.如权利要求1所述的早高强快速隧道锚杆锚索施工用粘合剂，其特征在于，所述减水剂为木质素磺酸钠盐减水剂、萘系高效减水剂、或聚羧酸减水剂中的一种或几种。3.如权利要求2所述的早高强快速隧道锚杆锚索施工用粘合剂，其特征在于，所述聚羧酸减水剂包括醚类或脂类聚羧酸减水剂的水剂或粉剂。4.如权利要求1所述的早高强快速隧道锚杆锚索施工用粘合剂，其特征在于，所述速凝剂为氯化锂或碳酸锂。5.如权利要求1所述的早高强快速隧道锚杆锚索施工用粘合剂，其特征在...
【专利技术属性】
技术研发人员：彭峰，张继昶，
申请(专利权)人：北京瑞威世纪铁道工程有限公司，
类型：发明
国别省市：北京,11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。