The invention discloses a mix design method for improving the flexural strength of aged fly ash aerated concrete. The mix design of aerated concrete blocks prepared with aged fly ash is as follows: cement: fly ash: water: glass fiber: aluminium powder: NaCl: microemulsion silicone polyether emulsion foam stabilizer: water reducer = 760:760:480:9:20:6:30. The mix design method of the invention can improve the flexural strength of the aged fly ash specimens, avoid damage during transportation, and a series of hidden dangers caused by insufficient flexural strength in future construction and daily use, such as breakage and partial shedding of the blocks caused by nailing in the aged fly ash aerated concrete blocks in daily life.
【技术实现步骤摘要】
提高陈积粉煤灰加气混凝土抗折强度的配合比设计方法
本专利技术属于轻质混凝土
，具体涉及提高陈积粉煤灰加气混凝土抗折强度的配合比设计方法。
技术介绍
粉煤灰是加气混凝土的主要原料。由于加气混凝土砌块的大量产出，造成新的粉煤灰不足以供应加气混凝土企业生产。为此，加气混凝土企业使用陈积粉煤灰代替新的粉煤灰，生产加气混凝土砌块。多家企业发现生产的陈积粉煤灰加气混凝土砌块在运输过程中由于抗折强度的不足，砌块数量损失在5％左右。可想而知，在该类砌块的在今后的砌筑、使用过程中还会存在由抗折强度不足所带来的安全隐患。为此需要研究一种提高陈积粉煤灰抗折强度的配合比方法。
技术实现思路
本专利技术的目的在于提供一种提高陈积粉煤灰加气混凝土抗折强度的配合比设计方法，以解决陈积粉煤灰代替新生产的粉煤灰去生产加气混凝土砌块，其抗折强度不足的技术问题。首先，本专利技术提出了一种提高陈积粉煤灰加气混凝土抗折强度的配合比设计方法，原材料之间的配合比关系是：水泥:粉煤灰:水:玻璃纤维:铝粉:NaCl:微乳型硅树脂聚醚乳液稳泡剂:减水剂＝760:760:480:9:8:20:6:30。其次，本专利...
【技术保护点】
1.一种提高陈积粉煤灰加气混凝土抗折强度的配合比设计方法，其特征在于：使用陈积粉煤灰制备加气混凝土砌块的配合比设计为：水泥:粉煤灰:水:玻璃纤维:铝粉:NaCl:微乳型硅树脂聚醚乳液稳泡剂:减水剂＝760:760:480:9:8:20:6:30。
【技术特征摘要】
1.一种提高陈积粉煤灰加气混凝土抗折强度的配合比设计方法，其特征在于：使用陈积粉煤灰制备加气混凝土砌块的配合比设计为：水泥:粉煤灰:水:玻璃纤维:铝粉:NaCl:微乳型硅树脂聚醚乳液稳泡剂:减水剂＝760:760:480:9:8:20:6:30。2.根据权利要求1所述的提高陈积粉煤灰加气混凝土抗折强度的配合比设计方法，其特征在于：所述使用陈积粉煤灰制备加气混凝土砌块步骤如下：1)将陈积粉煤灰在105℃下...
【专利技术属性】
技术研发人员：杨冬升，凌静，刘程鹏，谢礼兰，黄和维，李茂叶，赵玉印，岳廷旭，
申请(专利权)人：贵州师范大学，
类型：发明
国别省市：贵州,52