The invention relates to a method for preparing metal and sulfur by microwave decomposition of sulfide, belonging to the field of metal metallurgy and material preparation. The method utilizes microwave decomposition technology to optimize the process parameters of loading microwave, so that sulfide can be fully decomposed during the interaction between sulfide and microwave, thus obtaining high purity metal elements and sulfur, and avoiding the generation of harmful gases in the decomposition process. The method has the advantages of simple process, high production efficiency, environmental protection and low cost, and has broad application prospects in the field of metal metallurgy.
【技术实现步骤摘要】
一种微波分解硫化物制备金属和硫磺的方法
本专利技术涉及金属冶金及材料制备领域，具体涉及一种利用微波分解硫化物制备硫磺和有色金属的方法。
技术介绍
随着冶金技术的发展，目前提取硫化矿中金属(Mo，In，Ga，Pb，Mn，Zn，Ag，Ni，Pt，Fe等)的主要工艺为火法焙烧和湿法分解。这两种方法首先将硫化矿转化为金属氧化物(MeSx+O2→MeOx+SO2)、再利用中间产品进一步提纯为金属或金属化合物。在火法焙烧中不可避免产生污染环境的二氧化硫气体，随着环保要求的不断提高，虽然二氧化硫烟气制酸逐步成为硫酸的主要来源，但是硫酸制备的高投入和低价格，严重影响着有色冶金企业的经济效益；在湿法冶金过冲中普遍会用到酸碱及氨等，又因此形成了废水、废渣、废气等二次污染。因此，迫于环保要求和经济效益的双重压力下，新型的绿色冶金工艺开始受到众多研究者的关注。高能微波与材料相互作用具有加热速度快、加热均匀、有利于分解产生的蒸汽快速扩散等特点，已被开发应用在工业生产、科学研究、生物医学等领域。但是，以高能微波为热源直接使硫化物分解来获得硫磺和金属单质的研究目前尚无相关报道。
技术实现思路
针对...
【技术保护点】
1.一种微波分解硫化物制备金属和硫磺的方法，其特征在于：所述方法步骤如下，步骤1.将硫化物粉体均匀平铺在坩埚内，且平铺厚度不小于5mm，然后将坩埚放置在微波加热炉中，微波加热炉的进气口与保护气体的气源连接，微波加热炉的出气口与气体收集装置连接；步骤2.设定微波加热炉加载微波的微波功率为1000W～1600W以及加热温度为500℃～1100℃，并向微波加热炉内部充入流量为2L/min～20L/min不参与反应的保护气体；然后开始加载微波，达到加热温度后保温不少于10min，再停止加热并随炉冷却，最后停止通入保护气体，坩埚内的分解产物为金属和硫磺的混合物，气体收集装置中收集的产物为硫磺。
【技术特征摘要】
1.一种微波分解硫化物制备金属和硫磺的方法，其特征在于：所述方法步骤如下，步骤1.将硫化物粉体均匀平铺在坩埚内，且平铺厚度不小于5mm，然后将坩埚放置在微波加热炉中，微波加热炉的进气口与保护气体的气源连接，微波加热炉的出气口与气体收集装置连接；步骤2.设定微波加热炉加载微波的微波功率为1000W～1600W以及加热温度为500℃～1100℃，并向微波加热炉内部充入流量为2L/min～20L/min不参与反应的保护气体；然后开始加载微波，达到加热温度后保温不少于10min，再停止加热并随炉冷却，最后停止通入保护气体，坩埚内的分解产物为金属和硫磺的混合物，气体收集装置中收集的产物为硫磺。2.根据权利要求1所述的微波分解硫化物制备金属和硫磺的方法，其特征在于：所述硫化物为Mo...
【专利技术属性】
技术研发人员：舒永春，孙紫昂，朱锦鹏，郝振华，车玉思，何季麟，
申请(专利权)人：郑州大学，
类型：发明
国别省市：河南,41