The invention belongs to the technical field of magnesium-based sacrificial anode, in particular to a magnesium alloy containing Dy anode and its preparation method and application. The Dy-containing anode magnesium alloy is composed of the following components: 4.3-4.5% Al, 0.5-0.7% Zn, 0.8-1.2% Dy and the remainder is Mg. The Dy-containing anode magnesium alloy is prepared by induction furnace melting and metal mould casting. By adding rare earth element Dy to refine grain and improve structure, the invention has the characteristics of simple preparation process and uniform dissolution consumption, and is suitable for cathodic protection of steel parts in corrosive environment such as soil, seawater and water heater, and has broad application prospects.
【技术实现步骤摘要】
一种含Dy阳极镁合金及其制备方法与应用
本专利技术属于镁合金阳极
，具体涉及一种含Dy阳极镁合金及其制备方法与应用。
技术介绍
为了降低金属材料腐蚀带来的巨大经济损失，采用牺牲阳极进行电化学保护是一种有效的方法。金属镁具有较负的电极电位-2.37V(vsSHE)，负于铝的-2.31V和Zn-1.25V，因此，当使用镁及镁合金作为电源的阳极材料使用时，较负的电极电位可以为阳极的放电提供较大的驱动力，从而提供较大的放电电流。金属镁拥有较大的电容量，理论电容量为2205A.h/kg，更值得一提的是，金属镁的密度小，因此其拥有较大的质量能量密度，适合作为阳极材料放电使用。镁合金常被用作牺牲阳极材料，对重要设备装置的阴极材料(如钢)进行腐蚀防护，以延长阴极材料的使用寿命。但是，由于成分设计和制备工艺上的原因，普通镁合金阳极材料(如AZ31等)往往晶粒粗大，组织不均匀，且铝与镁形成网状Mg17Al12相，容易与镁基体形成微电池，使阳极材料的消耗不均匀，影响阳极材料的使用寿命。
技术实现思路
为了克服现有技术的不足和缺点，本专利技术的首要目的在于提供一种含Dy阳极镁合金，该镁...
【技术保护点】
1.一种含Dy阳极镁合金，其特征在于由如下按质量百分比计的组分组成：4.3～4.5％Al，0.5～0.7％Zn，0.8～1.2％Dy，余量为Mg。
【技术特征摘要】
1.一种含Dy阳极镁合金，其特征在于由如下按质量百分比计的组分组成：4.3～4.5％Al，0.5～0.7％Zn，0.8～1.2％Dy，余量为Mg。2.根据权利要求1所述的含Dy阳极镁合金，其特征在于由如下按质量百分比计的组分组成：4.5％Al，0.5％Zn，1.2％Dy，余量为Mg。3.权利要求1所述的含Dy阳极镁合金的制备方法，其特征在于包含如下步骤：将含Dy阳极镁合金各原料组分纯镁、纯铝、纯锌和镁-镝中间合金混合，熔炼铸造，得到含Dy阳极镁合金。4.根据权利要求3所述的含Dy阳极镁合金的制备方法，其特征在于：所述的原料组分的纯度为99.8％以上。5...
【专利技术属性】
技术研发人员：王莹，李萍，李聪灵，刘欢欢，张东晓，
申请(专利权)人：洛阳理工学院，
类型：发明
国别省市：河南,41
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。