The invention discloses a preparation method of an organic composite film and a method for improving its thermoelectric properties. The preparation method comprises mixing aniline with nano-carbon material, preparing a composite film of nano-carbon material and polyaniline by in-situ chemical oxidation polymerization and secondary doping of camphor sulfonic acid. The composite film of the nano-carbon material and polyaniline is an organic composite film. The method of improving the thermoelectric performance is: the organic composite membrane is immersed in alkali solution to remove doping, then washed with clean water to neutral and dried. Its preparation process is simple, low cost, high controllability and excellent stability. It is suitable for large-scale industrial production of organic composite thermoelectric materials.
【技术实现步骤摘要】
有机复合材料膜的制备方法及提高其热电性能的方法
本专利技术属于有机热电材料领域，涉及一种有机复合材料膜的制备方法及提高其热电性能的方法。
技术介绍
近年来环境污染和能源危机日益加剧，研究开发清洁能源及能源转换技术已经成为全球能源发展趋势。热电转换技术利用半导体材料的塞贝克效应，将生活和工业中的大量废弃热能回收并直接转换成电能再次使用，有效缓解化石能源消耗问题。同时热电器件对环境无污染，无机械运动部件，性能可靠，在航空航天、石油化工、微电子器件和可穿戴电子设备等领域有广泛的应用。因此，热电材料的开发成为新能源材料领域的研究热点。现今材料的热电性能由热电优值ZT来评价，ZT＝S2σT/κ,其中S为塞贝克系数，σ为电导率，T为绝对温度，κ为热导率，S2σ定义为功率因子，有机热电材料的热导率较低且变化较小，因此常采用功率因子衡量有机材料的热电性能。ZT值越高，材料的热电转换效率越高，更有利于实现热能向电能的高效转化。目前研究和使用的热电材料大多数为无机热电材料，其高温热电优值ZT大于2，但重金属污染、价格昂贵和可加工性差等缺点限制其推广应用。相对于无机热电材料，有机热电材...
【技术保护点】
1.一种有机复合材料膜的制备方法，其特征在于，将苯胺与纳米碳材料混合搅拌，通过原位化学氧化聚合和樟脑磺酸二次掺杂方法制备纳米碳材料与聚苯胺的复合薄膜，所述纳米碳材料与聚苯胺的复合薄膜即为有机复合材料膜。
【技术特征摘要】
1.一种有机复合材料膜的制备方法，其特征在于，将苯胺与纳米碳材料混合搅拌，通过原位化学氧化聚合和樟脑磺酸二次掺杂方法制备纳米碳材料与聚苯胺的复合薄膜，所述纳米碳材料与聚苯胺的复合薄膜即为有机复合材料膜。2.根据权利要求1所述有机复合材料膜的制备方法，其特征在于，所述纳米碳材料为具有纳米有序结构的碳材料。3.根据权利要求2所述有机复合材料膜的制备方法，其特征在于，所述纳米碳材料为碳纳米管、石墨烯或碳纤维。4.根据权利要求1-3任一项所述有机复合材料膜的制备方法，其特征在于，所述纳米碳材料的含量占所述有机复合材料膜的40-95wt％。5.一种提高如权利要求1-4任一项...
【专利技术属性】
技术研发人员：李鹏程，梁原，李慧，刘治田，高翔，彭祥，
申请(专利权)人：武汉工程大学，
类型：发明
国别省市：湖北,42
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。