The invention relates to a preparation method of polyurethane elastomer for spherical tire, which belongs to the field of polyurethane foaming, and is composed of two components A and B, in which component A is prepared from the following raw materials: polyether 100 500, polyester polyol 100 200, hydrolysis stabilizer 5 20, ultraviolet absorbent 5 20, and component B is prepared from the following raw materials: glass fiber 5 35, TDI: 50. 200 copies, chain extender 25 300 copies. The polyurethane material prepared by the invention can be applied to spherical tires with certain water absorption. When passing through watery pavement, the tire surface material will absorb water and become soft, increase friction, reduce skidding phenomenon and improve safety.
【技术实现步骤摘要】
球形轮胎用聚氨酯弹性体的制备方法
本专利技术涉及一种球形轮胎用聚氨酯弹性体的制备方法，属于聚氨酯发泡领域。
技术介绍
球形轮胎是汽车新革命的发展方向，相较于普通的轮胎，球形轮胎可360度无死角旋转，大大提高了汽车的机动灵活性，降低了翻车的可能，是未来汽车制动方式的发展方向。而目前市面上的球形轮胎用聚氨酯弹性体强度和耐磨性不是很高，同时材料基本上没有吸水性，这样势必就会影响轮胎和地面之间的摩擦力；本专利的所涉及的聚氨酯材料可应用于球形轮胎，具有较高的强度和耐磨性，且材料有一定的吸水性，在通过有水路面时轮胎表面材料会吸水变软，增加摩擦力，减少打滑现象，提高安全性。
技术实现思路
根据现有技术的不足，本专利技术要解决的技术问题是：提供一种球形轮胎用聚氨酯弹性体的制备方法，具有较高的强度和耐磨性，且材料有一定的吸水性，在通过有水路面时轮胎表面材料会吸水变软，增加摩擦力，减少打滑现象，提高安全性。本专利技术解决其技术问题所采用的技术方案是：提供一种球形轮胎用聚氨酯弹性体的制备方法，由A和B两组份构成，其中A组份由以下原料制备而成：聚醚100-500份，聚酯多元醇100-200份...
【技术保护点】
1.一种球形轮胎用聚氨酯弹性体的制备方法，其特征在于由A和B两组份构成，其中A组份由以下原料制备而成：聚醚 100‑500份，聚酯多元醇 100‑200份，水解稳定剂 5‑20份，紫外线吸收剂 5‑20份，B组份由以下原料制备而成：玻璃纤维 5‑35份，TDI 50‑200份，扩链剂 25‑300份。
【技术特征摘要】
1.一种球形轮胎用聚氨酯弹性体的制备方法，其特征在于由A和B两组份构成，其中A组份由以下原料制备而成：聚醚100-500份，聚酯多元醇100-200份，水解稳定剂5-20份，紫外线吸收剂5-20份，B组份由以下原料制备而成：玻璃纤维5-35份，TDI50-200份，扩链剂25-300份。2.根据权利要求1所述的球形轮胎用聚氨酯弹性体的制备方法，其特征在于所述的聚醚的官能度为3，分子量为1000-12000，伯羟基含量为5％-20％。3.根...