The invention discloses a method for using coatings for producing hydrogen storage alloys by vacuum induction melting, which includes: crushing the reaction slag in crucible to less than 150 micron, adding refractory binder in reaction slag, and adding water evenly; selecting sodium silicate or one or two mixtures of aluminum dihydrogen phosphate as refractory binder; The material is coated on the surface of refractory or ingot mould, and the refractory or ingot mould coated with the coating is heated to discharge water. The invention can isolate the contact and reaction between alloy melt and refractory or ingot mould, improve the quality of hydrogen storage alloy and the service life of ingot mould.
【技术实现步骤摘要】
真空感应熔炼生产储氢合金用涂层的使用方法
本专利技术涉及一种生产储氢合金的技术，具体是，涉及一种真空感应熔炼生产储氢合金用涂层的使用方法。
技术介绍
目前工业上生产储氢合金最常用的是中频真空电磁感应熔炼法，熔炼规模从几公斤至几吨不等，坩埚封闭在真空室中，利用电磁感应在坩埚盛装的金属(稀土、镍、钴、锰、铝等)导体内产生的涡旋电流加热炉料进行熔炼，在真空状态下进行金属与合金的冶炼并浇注，从而得到高质量的储氢合金，这种生产储氢合金的工艺方法叫真空感应熔炼法。坩埚是感应熔炼的重要组成部分，用于装料冶炼并起绝热、绝缘和传递能量的作用。生产储氢合金常用的坩埚为Al2O3坩埚、MgO坩埚或ZrO2坩埚。坩埚盛装的各种金属(稀土、镍、钴、锰、铝等)感应融化、合金化、精炼时，合金中的部分活性成分，特别是稀土在熔融阶段和坩埚接触面发生反应，形成炉渣，形成的炉渣很难与坩埚中的熔融状态合金再次发生反应，具有高温化学惰性。真空感应炉中还有引导合金熔液的部件，如流道、引流槽、上中间包、下中间包等部位都是耐火材料，材质主要有莫来石、刚玉、氧化镁、石墨等。高温熔融液体的金属活性高，特别是其中的稀...
【技术保护点】
1.一种真空感应熔炼生产储氢合金用涂层的使用方法，包括：将真空感应熔炼储氢合金时坩埚中的反应炉渣破碎至150μm以下，反应炉渣中添加耐火材料粘合剂，混合均匀添加水；耐火材料粘合剂选用水玻璃或者磷酸二氢铝的一种或者二者混合物；将混合物涂覆于耐火材料或锭模表面，涂覆了涂层的耐火材料或锭模经过加热将水排出。
【技术特征摘要】
1.一种真空感应熔炼生产储氢合金用涂层的使用方法，包括：将真空感应熔炼储氢合金时坩埚中的反应炉渣破碎至150μm以下，反应炉渣中添加耐火材料粘合剂，混合均匀添加水；耐火材料粘合剂选用水玻璃或者磷酸二氢铝的一种或者二者混合物；将混合物涂覆于耐火材料或锭模表面，涂覆了涂层的耐火材料或锭模经过加热将水排出。2.如权利要求1所述真空感应熔炼生产储氢合金用涂层的使用方法，其特征在于：每5份反应炉渣使用1-3份耐火材料粘合剂；水的加入量为：3～8份反应炉渣、耐火材料粘合剂，添加1份水。3.如...
【专利技术属性】
技术研发人员：李金，王利，闫慧忠，张旭，郑天仓，李宝犬，熊玮，周淑娟，赵玉园，徐津，
申请(专利权)人：包头稀土研究院，瑞科稀土冶金及功能材料国家工程研究中心有限公司，
类型：发明
国别省市：内蒙古,15