一种焊接方法和应用技术

本发明专利技术提供一种焊接方法和应用，焊接方法包括：将金属氧化物与合金紧贴后，升压升温至预设压力和预设温度；向所述金属氧化物与合金施加电场，得到金属氧化物‑合金焊接产物；其中，所述金属氧化物与正极连接，所述合金与负极连接。该焊接方法能够在低温的条件下实现金属氧化物与合金的快速焊接，并且在两者焊接的接口处不会生成合金金属的氧化物从而有效提高两者焊接接口的强度。

A Welding Method and Its Application

The invention provides a welding method and application. The welding method includes: after the metal oxide is closely attached to the alloy, the pressure is raised to the preset pressure and the preset temperature; the electric field is applied to the metal oxide and the alloy to obtain the welding product of the metal oxide and the alloy; the metal oxide is connected with the positive electrode, and the alloy is connected with the negative electrode. The welding method can realize rapid welding of metal oxides and alloys at low temperature, and the oxide of alloy metal will not be formed at the interface of the two welding, thus effectively improving the strength of the welding interface.

【技术实现步骤摘要】
一种焊接方法和应用
本专利技术涉及一种焊接方法和应用，属于焊接

技术介绍
金属氧化物，例如氧化锆(ZrO2)和氧化铝(Al2O3)等因为具有良好的力学性能，例如高强度以及断裂韧性，良好的化学稳定性和生物相容性而被用作生物材料，用来制造医疗器件、人造骨骼、牙齿等。然而，由于其脆性以及焊接可靠性差而导致其不能满足在生物方面的应用，因此通常需要与金属结合在一起使用以弥补其这方面的缺点。合金，例如钛合金由于其良好的生物相容性、抗腐蚀以及高的比强度而作为医疗以及生物材料领域最常见的金属材料。因此，氧化物与合金的焊接体已被广泛应用于制备生物材料和医学器件。目前关于氧化物与合金之间的焊接大多是在一定高温下通过直接的扩散焊接进行的，且需要较长的焊接时间且焊接强度不佳。以ZrO2和钛合金的焊接而言，由于钛元素具有很强的活性，并且其对氧有很强的亲和性，焊接时ZrO2中的氧元素和钛合金中的钛元素在高温下极易相互扩散并且发生化学反应而导致在ZrO2和钛合金之间的界面生成一层钛元素的氧化物，而生成的钛的氧化物具有很高的脆性而导致接口强度较低，因此在焊接时应该尽可能的避免形成钛氧化物。虽然通过钎焊的方本文档来自技高网...

【技术保护点】
1.一种焊接方法，其特征在于，包括：将金属氧化物与合金紧贴后，升压升温至预设压力和预设温度；向所述金属氧化物与合金施加电场，得到金属氧化物‑合金焊接产物；其中，所述金属氧化物与正极连接，所述合金与负极连接。

【技术特征摘要】
1.一种焊接方法，其特征在于，包括：将金属氧化物与合金紧贴后，升压升温至预设压力和预设温度；向所述金属氧化物与合金施加电场，得到金属氧化物-合金焊接产物；其中，所述金属氧化物与正极连接，所述合金与负极连接。2.根据权利要求1所述的焊接方法，其特征在于，所述预设温度为T且600≤T≤1000℃。3.根据权利要求1所述的焊接方法，其特征在于，所述预设压力为P且P≥1MPa，并且P小于所述金属氧化物的抗压强度和所述合金的抗压强度。4.根据权利要求1所述的焊接方法，其特征在于，所述电场的保持时间为0.5s-30min。5.根据权利要求1所述的焊接方法，其特征在于，所述将金属氧化物与合金紧贴前，...

【专利技术属性】
技术研发人员：王一光，
申请(专利权)人：北京理工大学，
类型：发明
国别省市：北京,11