A multidimensional synergistic modified polyimide composite material for ultrasonic motors is characterized by its main components as follows: polyimide 100, hydroxylated fullerene 0.1_1, multi-walled carbon nanotubes 0.1_3, graphene oxide 0.1_1. The preparation method is to mix the composite powder and add it into the hot-pressing mould. The molding temperature is 360-380 C, the pressure is 10-20MPa, the holding time is 60-90 minutes, and then the natural cooling demoulding. The composite material of the invention has high mechanical performance, stable friction coefficient and extremely low wear rate, and can greatly improve the bearing capacity, operation stability and service life of the ultrasonic motor.
【技术实现步骤摘要】
一种超声电机用多维协同改性聚酰亚胺复合材料及其制备方法
本专利技术属于聚合物复合材料领域，尤其是一种超声电机使用的复合材料，具体地说是一种超声电机用多维协同改性聚酰亚胺复合材料及其制备方法。
技术介绍
随着超声电机技术的不断发展及应用范围的扩大，对转子摩擦材料性能的要求越来越高，传统的聚四氟乙烯基复合材料由于机械强度低、硬度小、使用寿命短等缺点，很难满足超声电机高输出稳定性以及超长使用寿命。因此，发展新型摩擦材料对于超声电机的快速发展至关重要。目前旋转型超声电机使用的摩擦材料主要存在两大问题：一是摩擦性能不稳定，导致输出转速波动较大；二是在大载荷下使用寿命短，无法保证航空航天领域的长期运行。目前，国内还没有摩擦材料能完全解决以上两个问题。因此，寻求长寿命高稳定的摩擦材料是超声电机亟需解决的难题。首先，本专利技术选用“塑料之王”聚酰亚胺作为聚合物基体，因其是一种绝缘性能好、耐高温、耐腐蚀、耐磨损且承载能力很强的一种高分子材料，但是纯的聚酰亚胺很难满足超声电机高频微振动条件下的使用要求。所以对聚酰亚胺进行改性是提高其机械性能和摩擦学性能最有效的方法。本专利技术选用性能...
【技术保护点】
1.一种超声电机用多维协同改性聚酰亚胺复合材料，其特征在于它由聚酰亚胺、羟基化富勒烯、多壁碳纳米管和氧化石墨烯组成：各组份的质量份为：聚酰亚胺100份，羟基化富勒烯0.1‑1份， 多壁碳纳米管0.1‑3份，氧化石墨烯0.1‑1份。
【技术特征摘要】
1.一种超声电机用多维协同改性聚酰亚胺复合材料，其特征在于它由聚酰亚胺、羟基化富勒烯、多壁碳纳米管和氧化石墨烯组成：各组份的质量份为：聚酰亚胺100份，羟基化富勒烯0.1-1份，多壁碳纳米管0.1-3份，氧化石墨烯0.1-1份。2.根据权利要求1所述的超声电机用多维协同改性聚酰亚胺复合材料，其特征是所述的聚酰亚胺为微米级模压粉。3.根据权利要求2所述的超声电机用多维协同改性聚酰亚胺复合材料，其特征是所述的聚酰亚胺为75μm模压粉，它性能稳定，非常适合无机颗粒填充和模压。4.根据权利要求1所述的超声电机用多维协同改性聚酰亚胺复合材料，其特征是所述的羟基化富勒烯的羟基数为18-28，其表面大量的羟基能够与聚酰亚胺存在着强烈的氢键作用，提高了界面结合力；羟基化富勒烯在乙醇中分散性良好，避免了团聚现象，从而能够与聚酰亚胺和其他改性剂的良好分散。5.根据权利要求1所述的超声电机用多维协同改性聚酰亚胺复合材料，其特征是所述的多壁碳纳米管直径为8-15nm，长度为10-50μm，所述的多壁碳纳米管具有良好的力学性能，是提高聚合物强度的理想增强材料。6....
【专利技术属性】
技术研发人员：赵盖，宋敬伏，丁庆军，裘进浩，
申请(专利权)人：南京航空航天大学，
类型：发明
国别省市：江苏,32