The invention discloses a preparation method of secondary micro-structure to realize superhydrophobicity of material surface. The primary micro-structure surface is prepared with silica gel material on the matrix, and the prepared primary micro-structure is immersed in sodium hydroxide solution. After extraction, the residual sodium hydroxide solution on the matrix is completely removed by ultrasonic cleaning with absolute ethanol and deionized water, respectively. Substrate was dried and superhydrophobic secondary microstructural films were prepared. The preparation method of the invention utilizes sodium hydroxide solution to prepare secondary microstructures with simple process, mild reaction conditions, easy access to raw materials, no secondary pollution and low cost.
【技术实现步骤摘要】
一种实现材料表面超疏水性的二级微结构的制备方法
本专利技术涉及基体表面处理
，特别涉及材料表面超疏水性的二级微结构的制备方法。
技术介绍
超疏水表面由于其优异的防水性能，在国防、农业、工业生产和日常生活中有着广泛的应用前景，例如防止积雪、防雾、防污、防腐、自清洁、实现油水分离等。研究表明，材料表面的超疏水特性由材料表面微观结构和表面自由能共同决定，含有一定微纳米结构的低表面能材料可以极大地提高材料的超疏水性能。因此，在低表面能的材料表面构建超疏水微观结构，或在已经具有超疏水微观结构的表面上进行化学修饰降低其表面能成为了制备超疏水表面的重要方法。而相对于单一尺度的微观结构，例如西瓜叶、蝴蝶的眼角膜等，具有分级复合微纳米构型的表面更容易实现超疏水性，例如荷叶表面的微米乳突上存在着大量的纳米突起，这种微纳米分级结构是荷叶表面表现出超疏水性的根本原因。目前，制备分级复合微纳米构型的主要方法有很多种，例如模板法、等离子刻蚀法、溶胶-凝胶法、气相沉积法、相分离法等，这些方法通常需要更长的加工周期、复杂的仪器设备，成本高，难以大规模制备以及制备出的微结构大多大小不一、分布...
【技术保护点】
1.一种实现材料表面超疏水性的二级微结构的制备方法，其特征在于：包括以下步骤：1)在基体上用硅胶材料制备一级微结构表面，将制备好的一级微结构浸泡在氢氧化钠溶液中；2)取出后，分别用无水乙醇，去离子水超声清洗，把基体上残余的氢氧化钠溶液完全去除；3)用鼓风干燥箱对基体进行烘干处理；制得符合要求的超疏水性二级微结构薄膜。
【技术特征摘要】
1.一种实现材料表面超疏水性的二级微结构的制备方法，其特征在于：包括以下步骤：1)在基体上用硅胶材料制备一级微结构表面，将制备好的一级微结构浸泡在氢氧化钠溶液中；2)取出后，分别用无水乙醇，去离子水超声清洗，把基体上残余的氢氧化钠溶液完全去除；3)用鼓风干燥箱对基体进行烘干处理；制得符合要求的超疏水性二级微结构薄膜。2.如权利要求1所述的制备方法，其特征在于：步骤1)中所述的硅胶材料为聚二甲基硅氧烷PDMS。3.如权利要求1所述的制备方法，其特征在于：步骤1)中氢氧化钠溶液溶度为17-18mol/L；浸泡时间为6h。4.如权利要求1所述的制备方法，其特征在于：步骤2)中无水乙醇进行超声清洗时间为10-15min，再用去离子水超声清洗的时间为10-15min。5.如权利要求1所述的制备方法，其特征在于：步骤1)中一级微结构的具体制备方法为：i)将15-20...
【专利技术属性】
技术研发人员：吴化平，蒋坤鹏，孙申申，徐振雄，林森鹏，
申请(专利权)人：浙江工业大学，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。