The invention belongs to the technical field of thermosetting resins, and provides a trifunctional benzoxazine monomer based on resveratrol and its preparation method. The preparation method comprises mixing resveratrol, amine compound and polyformaldehyde, adding low polar solvent as reaction solvent, reacting at 80 130 (?) for 2 6 hours, filtering after reaction, washing the filtrate with water, then steaming and drying to obtain the filtrate. Products. The invention has the advantages of using biological phenol and synthesizing trifunctional benzoxazine monomer as the target product, simple synthesis steps, high yield, excellent thermal and mechanical properties, excellent flame retardancy, simple synthesis process, low requirements for equipment and suitable for large-scale production of cured benzoxazine resin.
【技术实现步骤摘要】
一种基于白藜芦醇的三官能苯并噁嗪单体及其制备方法
本专利技术属于热固性树脂
，尤其涉及一种基于生物基白藜芦醇的三官能苯并噁嗪单体及其制备方法。
技术介绍
苯并噁嗪聚合物是近年来开发的一类热固性聚合物，由于其相比于传统热固性树脂具有明显的优点而受到人们关注。苯并噁嗪树脂具有耐热性优秀、机械性能良好、聚合收缩接近于零、分子设计非常灵活、焦炭产率高、表面能较低等优良特性。在完全固化后，玻璃化转变温度高，具有很好的耐热性；苯并噁嗪在发生开环聚合后，具有与酚醛树脂相似的结构，这使得其电绝缘性能良好；将苯并噁嗪树脂在一定的温度下时，不需要任何催化剂便可发生固化。苯并噁嗪被广泛应用在模具压制、层压和树脂传递模型等一些成型加工工艺中；以及耐烧耐腐蚀材料、电子封装、机械制造业零件、航空航天材料、胶黏剂、电路板、真空泵旋片、绝缘材料等一些相关的生产领域。随着社会的发展，人们对于高性能材料的要求越来越高，这也是很多科研工作者和企业家的研究方向。其次，合成苯并噁嗪树脂的酚类化合物主要来自于石油，其分解产物对环境有一些危害，就可获得的石化产品原料和成本而言，苯并噁嗪树脂面临着与许多其...
【技术保护点】
1.一种基于白藜芦醇的三官能苯并噁嗪单体，其特征在于，分子式如下：
【技术特征摘要】
1.一种基于白藜芦醇的三官能苯并噁嗪单体，其特征在于，分子式如下：其中，为以下结构之一：2.根据权利要求1所述的一种基于白藜芦醇的三官能苯并噁嗪单体，其特征在于，所述基于白葫芦醇的三官能苯并噁嗪单体进一步固化交联后得到聚苯并噁嗪树脂，聚苯并噁嗪树脂在在氮气保护下热失重5％时温度为350-450℃，800℃时，残炭率为60-80％，燃烧热释放能为30-100Jg-1K-1。3.根据权利要求1所述的基于白藜芦醇的三官能苯并噁嗪单体的制备方法，其特征在于，具体包括以下步骤：将白藜芦醇，胺类化合物，多聚甲醛加入烧瓶中，加入低极性溶剂，在80-130℃反应2-6小时，停止反应后将反应物过滤，将滤液用水后旋蒸，烘干，得到...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。