The invention belongs to the field of 3D printing building materials, in particular to a desulfurized gypsum 3D printing alkali-activated cementitious material and its use method. By weight, the alkali-activated cementitious material comprises solid and liquid components, and the solid and liquid components are stored separately. The solid components include: slag 40-60 parts, desulfurization gypsum 20-50 parts, activator 0.02-0.05 parts, attapulgite 3-10 parts, thickener 0.1-0.5 parts and absorbent resin 1-5 parts. The liquid components include: 20-40 parts of water. The invention adopts desulfurized gypsum as the main raw material and coordinately regulates the setting and hardening rate and rheology of alkali-activated cementitious materials through additives to meet the extrusion requirements necessary for 3D printing. It can not only recycle desulfurized gypsum, reduce slag consumption and save cost, but also be widely used in 3D printing to develop efficient green building materials.
【技术实现步骤摘要】
一种脱硫石膏3D打印碱激发胶凝材料及其使用方法
本专利技术属于3D打印建筑材料领域,尤其涉及一种使用脱硫石膏与矿渣废弃物并通过触变剂和粘度改性剂来调控3D打印结构稳定性和提高力学性能的碱激发胶凝材料。
技术介绍
本专利技术
技术介绍
中,公开的信息仅仅旨在增加对本专利技术的总体背景的理解,而不必然被视为承认或以任何形式暗示该信息构成已经成为本领域一般技术人员所公知的现有技术。与传统的建筑技术相比,3D打印建筑技术具备环保、绿色和低成本的优点,能够大大提高生产效率,并且很容易打印弯曲和复杂建筑。但目前所使用的胶凝材料主要为水泥基材料,其是能源消耗和CO2排放的主要来源。大量的水泥等建筑材料的消耗要求我们必须合理改善建筑能耗所带来的问题,如何高效的发展绿色建筑使得建筑节能成为亟需解决问题之一。碱激发胶凝材料,又称碱激发水泥,是由碱性的激发剂激发具有潜在活性的工业废渣制备而成,因此碱激发胶凝材料制备能耗低,能够大量消耗工业废渣,其研究与应用因而发展较快。然而,3D打印碱激发胶凝材料较快的凝结时间和难以调控的流变性能造成其打印后的结构稳定性较差,且难以在3D打印技术中进行应用 ...
【技术保护点】
1.一种脱硫石膏3D打印碱激发胶凝材料,其特征在于:以重量份计,所述碱激发胶凝材料包括固态组分和液态组分,且所述固态组分和液态组分分开存放,其中:所述固态组分包括:矿渣40~60份、脱硫石膏20~50份、激发剂0.02~0.05份、凹土3~10份、增稠剂0.1~0.5份、吸水树脂1~5份;所述液态组分包括:水20~40份。
【技术特征摘要】
1.一种脱硫石膏3D打印碱激发胶凝材料,其特征在于:以重量份计,所述碱激发胶凝材料包括固态组分和液态组分,且所述固态组分和液态组分分开存放,其中:所述固态组分包括:矿渣40~60份、脱硫石膏20~50份、激发剂0.02~0.05份、凹土3~10份、增稠剂0.1~0.5份、吸水树脂1~5份;所述液态组分包括:水20~40份。2.如权利要求1所述的脱硫石膏3D打印碱激发胶凝材料,其特征在于:以重量份计,所述碱激发胶凝材料包括以下组分:固态组分包括:矿渣40~50份、脱硫石膏22~35份、激发剂0.02~0.04份、凹土3~7份、增稠剂0.3~0.5份、吸水树脂1~3份;液态组分包括:水20~40份。3.如权利要求1所述的脱硫石膏3D打印碱激发胶凝材料,其特征在于:以重量份计,所述碱激发胶凝材料包括以下组分:固态组分包括:矿渣40~50份、脱硫石膏22~35份、激发剂0.02~0.04份、凹土3~7份、增稠剂0.3~0.5份、吸水树脂2~5份;液态组分包括:水20~40份。4.如权利要求1-3任一项所述的脱硫石膏3D打印碱激发胶凝材料,其特征在于:所述固态组分的存在形式包括:每一种固态组分单独存在。5.如权利要求1-3任一项所述的脱硫石膏3D打印碱激发胶凝材料,其特征在于:所述固态组分的存在形式包括:将其中的任意两种或两种以上的固态组分混合。6.如权利要求4所述的脱硫石膏3D打印碱激发胶凝材料,其特征在于:所述碱激发剂为:水玻璃、硫酸钠和磷酸钠的混合物,且水玻璃、硫酸钠、磷酸钠的质量...
【专利技术属性】
技术研发人员:芦令超,陈明旭,李来波,赵丕琪,王守德,宫晨琛,
申请(专利权)人:济南大学,
类型:发明
国别省市:山东,37