The invention relates to a porous mortar with embedded composite sacrificial anode for corrosion protection and repair of reinforced concrete structures and a preparation method thereof, belonging to the field of cathodic protection. Mortar with high porous structure was obtained by adding pore-forming agent and stabilizer. Compared with the prior art, the porous mortar of the present invention can not only greatly enhance the activation effect of sacrificial anode in concrete environment, but also have high capacity for corrosion products produced by the anode, and can effectively alleviate the volume expansion effect of corrosion products.
【技术实现步骤摘要】
一种埋入式复合牺牲阳极多孔砂浆及其制备方法
本专利技术属于阴极保护领域，涉及一种用于海工钢筋混凝土结构腐蚀防护与修复的埋入式复合牺牲阳极的多孔砂浆及其制备方法。
技术介绍
混凝土中钢筋的腐蚀被认为是导致混凝土结构耐久性下降的首要原因。在恶劣的海洋环境下，混凝土中钢筋发生腐蚀的主要原因是Cl-的侵蚀。钢筋混凝土中的高碱环境使得钢筋表面生成一层致密的钝化膜，从而保护钢筋基本不被腐蚀。当海洋环境中所含有的Cl-会伴随着海水通过混凝土的毛细孔渗透到钢筋表面时，Cl-会阻碍钢筋表面形成钝化膜，大大降低溶液中的电阻，并与铁离子生成可溶性盐，造成铁基体去极化作用发生的腐蚀溶解速度大于极化作用生成钝化膜的速度，从而导致铁基体发生腐蚀。钢筋的腐蚀不仅会使钢筋断面损失而导致钢筋强度降低，增加钢筋发生应力腐蚀断裂的可能性，还会使钢筋与混凝土的握裹力下降。钢筋腐蚀所产生的铁锈的最大体积将超过其原体积的6倍，产生的膨胀应力高达60MPa，使混凝土发生胀裂。并且高温、高湿和高盐度的环境条件将会促进混凝土中钢筋腐蚀的动力学过程，显著地加速上述腐蚀过程的进行，从而加速混凝土耐久性的劣化。处在潮差...
【技术保护点】
1.一种用于海工钢筋混凝土结构腐蚀防护与修复的埋入式复合牺牲阳极的多孔砂浆，其特征在于，多孔砂浆包覆于金属牺牲阳极外部，其组成包含水泥、骨料及活性盐；通过添加复合造孔剂获得的多孔砂浆的孔隙率为30‑65％。
【技术特征摘要】
1.一种用于海工钢筋混凝土结构腐蚀防护与修复的埋入式复合牺牲阳极的多孔砂浆，其特征在于，多孔砂浆包覆于金属牺牲阳极外部，其组成包含水泥、骨料及活性盐；通过添加复合造孔剂获得的多孔砂浆的孔隙率为30-65％。2.根据权利要求1所述的多孔砂浆，其特征在于，所述的多孔砂浆中的水泥为硅酸盐、硫铝酸盐、铁铝酸盐、高铝酸盐或磷酸盐类水泥。3.根据权利要求1所述的多孔砂浆，其特征在于，所述的多孔砂浆中的骨料为颗粒大小在0.2-1mm范围内的细砂或粉煤灰。4.根据权利要求1所述的多孔砂浆，其特征在于，所述的多孔砂浆中的活性盐为碱金属氢氧化物或碱金属碳酸盐。5.根据权利要求1所述的多孔砂浆，其特征在于，所述的多孔砂浆在制备时的灰砂比为(0.3～3)：1，水灰比为(0.5～1.2):1。6.根据权利要求1所述的多孔砂浆，其特征在于，所述的复合造孔剂为强氧化性碱性水溶液或固体粉末；当复合造孔剂为碱性水溶液时，其含量为砂浆固料质量的1％～7％，当复合造孔剂为固态粉末时，其含量为砂浆固料质量的0.15％～1％；所述的固态粉末状的复合造孔剂，其粉末的颗粒小于...
【专利技术属性】
技术研发人员：赵相玉，秦铁男，王亚东，
申请(专利权)人：南京优邦加能新材料科技有限公司，
类型：发明
国别省市：江苏,32