A method for preparing isobutyraldehyde catalyst relates to a method for preparing catalyst. The invention relates to a method for preparing catalyst for synthesizing isobutyraldehyde from methanol and ethanol or propanol. It includes the following steps: dissolving a certain amount of vanadate, citric acid and two or three nitrates such as Fe, Cu, Ni, Zr, Ca and Ce in aqueous solution, then steaming the mixed solution at high temperature in a constant temperature water bath pot, polar drying at 100 120 and calcining at 400 600 in a muffle furnace to prepare unique V_Fe_M_N (M is Cu or Ni, N is Zr, Ca and C). A) structured solid catalyst. The catalyst has good catalytic performance in the one-step synthesis of isobutyraldehyde from methanol with ethanol or propanol.
【技术实现步骤摘要】
一种制备异丁醛催化剂方法
本专利技术涉及一种制备催化剂方法，特别是涉及一种制备异丁醛催化剂方法。
技术介绍
异丁醛是一种重要的有机化工原料，应用比较广泛，通过它可以制备出的下游产品颇多，且均应用较为广泛，随着工业化的发展，对异丁醛的需求量越来越大。而目前工业上生产异丁醛的方式是羰基合成法制备正丁醇时产生的副产物，它的生产线是以石油资源为主要原料，这不仅使异丁醛的收率较低，而且原料也因资源匮乏会受阻，因此研究新的制备异丁醛的生产路线是必不可少的。经过不断的探究发现，利用以煤化工为原料来源的甲醇乙醇可以通过一步法合成异丁醛。我国的煤炭资源非常丰富，而此方法使用的原料甲醇和乙醇均可由煤炭制备，大大减少了原料的成本，也可以合理的应用我国的煤炭资源。本论文的研究目的在于开发新的催化剂，提高催化剂的催化活性，以提高乙醇转化率和异丁醛的选择性。宁波大学固体材料研究所的陈凯文[80]等采用浸渍法制备了催化剂CuO-MnO/Al2O3和CuO-MnO/SiO2，在常压和不同温度条件下考察了催化剂对甲醇、乙醇一步合成异丁醛的催化性能。采用CuO-MnO/Al2O3催化剂时发现，在反应...
【技术保护点】
1.一种制备异丁醛催化剂方法，其特征在于，所述方法包括以下制备过程：将钒酸盐和柠檬酸配置成水溶液，根据需求添加不同含量的Fe，同时加入Cu、Ni、Ce、Zr、Ca中的一种或两种金属可溶性盐分别配置成水溶液，把这两种溶液进行混合，在恒温水浴锅中进行加热蒸干，然后移至干燥箱干燥，马弗炉煅烧，得到固体催化剂，根据装样催化剂所需的颗粒大小进行过筛待用即可；其中所述的V金属盐为钒可溶性盐， Fe、Cu、Ni、Ce、Zr和Ca一种等相应的硝酸盐；其中恒温水浴锅温度为70‑90℃，干燥的温度为100‑120℃，煅烧温度为400‑600℃。
【技术特征摘要】
1.一种制备异丁醛催化剂方法，其特征在于，所述方法包括以下制备过程：将钒酸盐和柠檬酸配置成水溶液，根据需求添加不同含量的Fe，同时加入Cu、Ni、Ce、Zr、Ca中的一种或两种金属可溶性盐分别配置成水溶液，把这两种溶液进行混合，在恒温水浴锅中进行加热蒸干，然后移至干燥箱干燥，马弗炉煅烧，得到固体催化剂，根据装样催化剂所需的颗粒大小进行过筛待用即可；其中所述的V金属盐为钒可溶性盐，Fe、Cu、Ni、Ce、Zr和Ca一种等相应的硝酸盐；其中恒温水浴锅温度为70-90℃，干燥的温度为100-120℃，煅烧温度为400-600℃。2.根据权利要求1所述的一种制备异丁醛催化剂方法，其...
【专利技术属性】
技术研发人员：王康军，董玉，范旭萌，张雅静，许光文，丁茯，
申请(专利权)人：沈阳化工大学，
类型：发明
国别省市：辽宁,21