The present invention discloses a new process for bright coating on environmentally friendly metal surfaces, including: a metal base and a bright coating on the surface of the metal base. The metal base is pig iron base and the bright coating is chromium alloy coating. The chromium alloy coating contains 70 75 parts of chromium powder, 15 20 parts of aluminium powder, 1 4 parts of binder and 6 9 parts of dispersant. The chromium alloy coating is prepared by mixing, grinding, dispersing, spraying, drying and firing chromium powder, aluminium powder, binder and dispersant. By the above way, the invention coats a bright chromium alloy coating on the pig iron surface, which can enhance the gloss of the pig iron surface and has the function of rust prevention.
【技术实现步骤摘要】
环保型金属表面光亮新工艺
本专利技术涉及金属涂层领域,特别是涉及环保型金属表面光亮镀膜新工艺。
技术介绍
涂层是指附着在某一基体材料上起某种特殊作用,且与基体材料具有一定结合强度的薄层材料。它可以克服基体材料的某种缺陷,改善其表面特性,如光学特性、电学特性、耐侵蚀及腐蚀、耐磨损性和提高机械强度等,它属于一种有支撑体的薄膜。工业上,通常采用电镀方式在基体表面镀上一层其他金属或合金,来达到或改善对基体金属的表面光泽度,提高其耐磨、耐腐蚀等性能。电镀金属或合金的性能直接影响基体的表面质量,同时传统的电镀工艺十分复杂,并且会产生有害物质,其工艺成本高且不安全环保。
技术实现思路
本专利技术主要解决的技术问题是提供环保型金属表面光亮镀膜新工艺,在生铁表面包覆一层光亮铬合金涂层,能够增强生铁表面光泽度,同时具有防锈作用。为解决上述技术问题,本专利技术采用的一个技术方案是:提供环保型金属表面光亮镀膜新工艺,包括:金属基体和位于所述金属基体表面的光亮涂层,所述金属基体为生铁基体,所述光亮涂层为铬合金涂层,所述铬合金涂层包含的成分及其质量份数为:铬粉70-75份、铝粉15-20份、粘结剂1-4份、分散剂6-9份,所述铬合金涂层是由铬粉、铝粉、粘结剂和分散剂经混合、研磨分散、喷涂、烘干、烧制而成的。在本专利技术一个较佳实施例中,所述铬粉和铝粉的粒径均为70-80nm。在本专利技术一个较佳实施例中,所述铬合金涂层的厚度为1-2mm。本专利技术的有益效果是:本专利技术环保型金属表面光亮镀膜新工艺,在生铁基体表面包覆一层光亮铬合金涂层,该光亮铬合金镀层是由配比合理的铬粉、铝粉、粘结剂和 ...
【技术保护点】
1.环保型金属表面光亮镀膜新工艺,其特征在于,包括:金属基体和位于所述金属基体表面的光亮涂层,所述金属基体为生铁基体,所述光亮涂层为铬合金涂层,所述铬合金涂层包含的成分及其质量份数为:铬粉70‑75份、铝粉15‑20份、粘结剂1‑4份、分散剂6‑9份,所述铬合金涂层是由铬粉、铝粉、粘结剂和分散剂经混合、研磨分散、喷涂、烘干、烧制而成的。
【技术特征摘要】
1.环保型金属表面光亮镀膜新工艺,其特征在于,包括:金属基体和位于所述金属基体表面的光亮涂层,所述金属基体为生铁基体,所述光亮涂层为铬合金涂层,所述铬合金涂层包含的成分及其质量份数为:铬粉70-75份、铝粉15-20份、粘结剂1-4份、分散剂6-9份,所述...