The invention discloses an efficient method for preparing alloy zinc bars, which comprises the following steps: adding copper, sodium and zinc into industrial furnace for smelting; gradually adding zinc ingots until the composition requirements are met, in which the mass percentage content of copper is 0.1 2%, the mass percentage content of sodium is 0.05 0.1%, and the rest is said zinc; adding refining agent for stirring refining; and refining the finished alloy. The temperature of the melt is controlled at 450 500 C, and the alloy zinc rod is obtained by pressure extrusion. The alloy zinc bars prepared by this method can be drawn into different lengths, diameters and shapes according to the requirements. The mechanical properties and corrosion resistance of the alloy zinc bars are similar to those of brass bars, and the cost is greatly reduced.
【技术实现步骤摘要】
一种高效制备合金锌棒的方法
本专利技术涉及一种锌棒制备
，特别涉及一种铜钠锌合金锌棒。
技术介绍
黄铜棒被广泛的应用于空调管、冰箱管、机油管、给水管道以及各种机械配套用料，但是铜的价格居高不下，导致黄铜棒的成本很高。使用一种价格较低的金属棒材代替黄铜棒，已成为行业内共同面对的难题。
技术实现思路
本专利技术的目的是提供一种高效制备合金锌棒的方法，该制备方法得到的合金锌棒可以根据需求拉成不同长度、直径、形状，其机械性能、抗腐蚀性能与黄铜棒相当，成本得到大幅度下降。本专利技术提供一种高效制备合金锌棒的方法，包含以下步骤：S1、将铜、钠和锌加入工业炉进行熔炼；S2、逐步加入锌锭，直到达到成分要求，其中铜的质量百分含量为0.1-2％，钠的质量百分含量为0.05-0.1％，其余为所述锌；S3、加入精炼剂，进行搅拌精炼；S4、将精炼完成的合金熔液进行保温，温度控制在450-500℃；S5、通过挤压、刨皮、拉丝，得到合金锌棒。该制备方法得到的铜钠锌合金锌棒，使用时，机械性能、抗腐蚀性能与黄铜棒相当，但是成本得到大幅度下降。在一些实施方式中，还包括加入0.1-0.2％的稀土进行...
【技术保护点】
1.一种高效制备合金锌棒的方法，其特征在于，包含以下步骤：S1、将铜、钠和锌加入工业炉进行熔炼；S2、逐步加入锌锭，直到达到成分要求，其中铜的质量百分含量为0.1‑2％，钠的质量百分含量为0.05‑0.1％，其余为所述锌；S3、加入精炼剂，进行搅拌精炼；S4、将精炼完成的合金熔液进行保温，温度控制在450‑500℃；S5、通过挤压、刨皮、拉丝，得到合金锌棒。
【技术特征摘要】
1.一种高效制备合金锌棒的方法，其特征在于，包含以下步骤：S1、将铜、钠和锌加入工业炉进行熔炼；S2、逐步加入锌锭，直到达到成分要求，其中铜的质量百分含量为0.1-2％，钠的质量百分含量为0.05-0.1％，其余为所述锌；S3、加入精炼剂，进行搅拌精炼；S4、将精炼完成的合金熔液进行保温，温度控制在450-500℃；S5、通过挤压、刨皮、拉丝，得到合金锌棒。2.根据权利要求1所述的一种高效制备合金锌棒的方法，其特征在于，还包括加入0.1-0.2％的...