本发明专利技术提供一种硅灰石复合填料的制备方法，将偏硅酸钠、石墨烯、硅灰石及聚乙二醇放入乙醇水溶液中并滴加氯化铵溶液，经过离心、过滤、干燥、粉碎，即制得硅灰石复合填料。硅灰石表面经纳米SiO2及石墨烯包覆后其锐利的棱角变得钝化，平滑的表面也变的粗糙，缓解了由此造成的复合材料内局部应力集中的问题。同时包覆在硅灰石表面的纳米SiO2还增强了填料与聚烯烃基体之间的界面作用力，从而提升聚烯烃复合材料的力学性能。

A preparation method of wollastonite composite filler

The invention provides a preparation method of wollastonite composite filler. Sodium metasilicate, graphene, wollastonite and polyethylene glycol are put into ethanol aqueous solution and dripped with ammonium chloride solution. After centrifugation, filtration, drying and crushing, wollastonite composite filler is prepared. The sharp edges and corners of wollastonite coated with nano-SiO 2 and graphene become passive, and the smooth surface becomes rough, which alleviates the problem of local stress concentration in the composites. At the same time, nano-SiO 2 coated on wollastonite surface also enhances the interfacial force between filler and polyolefin matrix, thereby improving the mechanical properties of polyolefin composites.

【技术实现步骤摘要】
一种硅灰石复合填料的制备方法
本专利技术属于高分子材料
，特别是指一种硅灰石复合填料的制备方法。
技术介绍
硅灰石作为高分子材料领域中被广泛应用于填料，硅灰石增韧增强聚合物是近年来新研究开发出来的一种热门技术，即通过硅灰石加入到聚合物中，能够较大的提高聚合物的韧性及强度。专利技术人通过在本领域多年的生产实践，得到一种通过硅灰石填料来改性聚烯烃的技术，该技术同现有技术直接使用硅灰石改性聚烯烃，不论是韧性还是强度均有大幅度的提高，这对于扩展聚烯烃复合材料的应用领域，具有非常现实的意义。
技术实现思路
本专利技术的目的是提供一种硅灰石复合填料的制备方法，较现有技术硅灰石为填料改性聚烯烃韧性及强度均有较大的提高。本专利技术是通过以下技术方案实现的：一种硅灰石复合填料的制备方法，包括以下步骤：1)将硅灰石在80-100℃的烘箱中干燥3-5h，充分去除硅灰石表面的吸附水以备用；(2)将偏硅酸钠、石墨烯、硅灰石及聚乙二醇放入乙醇水溶液中，于温度为90-110℃的恒温水浴锅中8-10h后使硅灰石完全溶解；(3)在电动搅拌器搅拌下缓慢滴加饱和氯化铵溶液，静置2-4h后离心、过滤、干燥、粉碎，即制得硅本文档来自技高网...

【技术保护点】
1.一种新型硅灰石复合填料的制备方法，其特征在于，包括以下步骤：(1)将硅灰石在80‑100℃的烘箱中干燥3‑5h，充分去除硅灰石表面的吸附水以备用；(2)将偏硅酸钠、石墨烯、硅灰石及聚乙二醇放入乙醇水溶液中，于温度为90‑110℃的恒温水浴锅中8‑10h后使硅灰石完全溶解；(3)在电动搅拌器搅拌下缓慢滴加饱和氯化铵溶液，静置2‑4h后离心、过滤、干燥、粉碎，即制得硅灰石复合填料。

【技术特征摘要】
1.一种新型硅灰石复合填料的制备方法，其特征在于，包括以下步骤：(1)将硅灰石在80-100℃的烘箱中干燥3-5h，充分去除硅灰石表面的吸附水以备用；(2)将偏硅酸钠、石墨烯、硅灰石及聚乙二醇放入乙醇水溶液中，于温度为90-110℃的恒温水浴锅中8-10h后使硅灰石完全溶解；(3)在电动搅拌器搅拌下缓慢滴加饱和氯化铵溶液，静置2-4h后离心、...

【专利技术属性】
技术研发人员：严静儿，
申请(专利权)人：严静儿，
类型：发明
国别省市：浙江,33