The invention discloses a preparation method of a flame-retardant and impact-resistant printing base film, which relates to the technical field of the base film. The invention consists of the following raw materials: PVC resin 80 100, EVA 10 15, CPE 10 15, organotin stabilizer 5 10, MBS resin 4 6, internal lubricant 3 6, external lubricant 4 6, ACR additive 2 4. The coating solution prepared by using SiO 2 and nano-alumina as raw materials can form a composite structure of alloying layer on the printing base film. The flame retardant properties and structural strength of the printing base film were significantly improved, which made it more resistant to external shocks.
【技术实现步骤摘要】
阻燃、抗冲击印刷基膜的制备方法
：本专利技术涉及基膜
，具体涉及阻燃、抗冲击印刷基膜的制备方法。
技术介绍
：现有技术中，常见的地面装饰材料有瓷砖、木地板或地毯等，其原材料多来自天然，长期过度的开发自然资源，对生态环境造成的影响不可小视；随着人们生活水平的提高，地面装饰材料需求量随之增长，如何既能有效开发和综合利用自然资源，符合节能环保的基本准则，又能使地面装饰材料美观大方、经济实用、满足人们的不同使用目的并具有一定的舒适性，采用复合、合成等方式生产地面装饰材料已是大势所趋。PVC地板是当今世界上非常流行的一种新型轻体地面装饰材料，是一种在欧美及亚洲的日韩广受欢迎的产品，风靡国外，从80年代初开始进入中国市场，至今在国内的大中城市已经得到普遍的认可，使用非常广泛，可以运用在各种场所如家庭、医院、办公楼、工厂、超市等。PVC地板是指采用聚氯乙烯材料生产的地板，以聚氯乙烯及其共聚树脂为主要原料，加入填料、增塑剂、稳定剂、着色剂等辅料，在片状连续基材上，经涂敷工艺或经压延、挤出或挤压工艺生产而成，PVC地板及其衍生地板已经越来越受到广大消费者的喜爱，使用也越来越广...
【技术保护点】
1.阻燃、抗冲击印刷基膜的制备方法，其特征在于，包括以下步骤：(1)将PVC树脂80‑100份、EVA 10‑15份、CPE 10‑15份、有机锡稳定剂5‑10份、MBS树脂4‑6份、内润滑剂3‑6份、外润滑剂4‑6份、ACR助剂2‑4份，放入混合机中混合；(2)进行密炼、压延、冷却、入库养生12小时，形成印刷基膜；(3)在印刷基膜上进行铺膜，然后在硫化机中进行烧制，制得半成品；(4)将半成品养生12小时；(5)检验、分切、收卷、包装。
【技术特征摘要】
1.阻燃、抗冲击印刷基膜的制备方法，其特征在于，包括以下步骤：(1)将PVC树脂80-100份、EVA10-15份、CPE10-15份、有机锡稳定剂5-10份、MBS树脂4-6份、内润滑剂3-6份、外润滑剂4-6份、ACR助剂2-4份，放入混合机中混合；(2)进行密炼、压延、冷却、入库养生12小时，形成印刷基膜；(3)在印刷基膜上进行铺膜，然后在硫化机中进行烧制，制得半成品；(4)将半成品养生12小时；(5)检验、分切、收卷、包装。2.根据权利要求1所述的阻燃、抗冲击印刷基膜的制备方法，其特征在于，所述铺膜液的制备方法包括以下步骤：(1)柔性石墨的改性：将柔性石墨加入到去离子水中，搅拌均匀后，加入硅烷偶联剂和链增长剂，加热至回流状态保温搅拌0.5-2h，趁...
【专利技术属性】
技术研发人员：胡伟，吴磊，张德顺，李汪洋，陈辉，王成爱，孙天龙，范守贵，赵凯，
申请(专利权)人：安徽嘉阳新材料科技有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。