The invention relates to the preparation method of polyformaldehyde dimethyl ether, which mainly solves the problems of low catalyst activity and low selectivity in the process of synthesizing polyformaldehyde dimethyl ether by using methanol, formaldehyde and polyformaldehyde as raw materials in the existing technology. The preparation method of polyformaldehyde dimethyl ether includes methanol, formaldehyde and polyformaldehyde as raw materials, methanol:formaldehyde:poly-formaldehyde. The mass ratio of formaldehyde is (0-10):1, the amount of methanol and formaldehyde can not be equal to 0 at the same time. The raw material contacts with the catalyst to produce polyformaldehyde dimethyl ether. The catalyst is a cationic exchange resin modified by metal ions. The modified metal includes the technical scheme of IIA metal, which can be used in the industrial production of polyformaldehyde dimethyl ether.
【技术实现步骤摘要】
聚甲醛二甲醚的制备方法
本专利技术涉及聚甲醛二甲醚的制备方法。
技术介绍
近年来，随着工业革命影响日趋深入和我国特有的“多煤、少油、有气”的资源格局，我国石油资源日益紧张，石油供给压力空前增大。预计未来10～20年，我国石油供给率只有～50％。如何利用我国丰富的煤炭资源解决我国的能源危机便成为科研工作者急需解决的问题。因此由煤基甲醇开发新型的油品替代品日益受到人们的重视。二甲醚最早被提出作为一种柴油的添加剂，然而由于其自身冷启动性能差、常温下蒸汽压高、容易产生气阻使得二甲醚作为车用替代燃料的成本明显升高。聚甲醛二甲醚，即Polyoxymethylenedimethylethers(PODE)，是一类物质的通称，其简式可以表示为CH3O(CH2O)nCH3，具有较高的辛烷值(>30)和氧含量(42～51％)。当n的取值为2～10时，其物理性质、燃烧性能与柴油非常接近，较好的解决了二甲醚作为车用柴油调和组分存在的缺陷。因此聚甲醛二甲醚可作为新型的清洁柴油组分，在柴油中的添加量可达30％(v/v)，可以改善柴油在发动机中的燃烧状况，提高热效率，降低尾气中的颗粒物以...
【技术保护点】
1.聚甲醛二甲醚的制备方法，包括，以甲醇、甲缩醛和多聚甲醛为原料，其中甲醇∶甲缩醛∶多聚甲醛的质量比为(0～10)∶(0～10)∶1，甲醇与甲缩醛的用量不能同时为0，原料与催化剂接触，反应生成聚甲醛二甲醚，所述催化剂为金属离子改性的阳离子交换树脂，所述改性金属包括IIA金属。
【技术特征摘要】
1.聚甲醛二甲醚的制备方法，包括，以甲醇、甲缩醛和多聚甲醛为原料，其中甲醇∶甲缩醛∶多聚甲醛的质量比为(0～10)∶(0～10)∶1，甲醇与甲缩醛的用量不能同时为0，原料与催化剂接触，反应生成聚甲醛二甲醚，所述催化剂为金属离子改性的阳离子交换树脂，所述改性金属包括IIA金属。2.根据权利要求1所述的方法，其特征是催化剂用量为原料重量的0.05～10％。3.根据权利要求1所述的方法，其特征是反应温度为70～200℃。4.根据权利要求1所述的方法，其特征是反应压力为0.2～6MPa。5.根据权利要求1...
【专利技术属性】
技术研发人员：高晓晨，石竹，柏诗哲，
申请(专利权)人：中国石油化工股份有限公司，中国石油化工股份有限公司上海石油化工研究院，
类型：发明
国别省市：北京,11