The invention relates to a preparation method of multistage hydrophobic and hydrophobic double-layer membrane for membrane distillation, which consists of beaded polyvinylidene fluoride nanofiber membrane as hydrophobic layer and dendritic polyvinylidene fluoride nanofiber membrane as hydrophilic layer. Its characteristics include: 1) configuration of spinning solution; 2) preparation of hydrophobic double-layer membrane for membrane distillation. The multi-stage hydrophobic and hydrophobic bilayer membrane for membrane distillation prepared by the invention has larger permeation flux and has broad application prospects in the field of membrane distillation.
【技术实现步骤摘要】
一种膜蒸馏用多级结构亲疏水双层膜的制备方法
本专利技术涉及一种膜蒸馏用多级结构亲疏水双层膜的制备方法，具体涉及采用静电纺丝技术在亲水聚偏氟乙烯树枝状纳米纤维膜上纺制一层不同厚度的串珠结构氟改性丙烯酸酯共聚物掺杂聚偏氟乙烯(PVDF)纳米纤维膜作为疏水层，制得膜蒸馏用多级结构亲疏水双层膜，属于功能高分子纤维
技术背景膜蒸馏技术作为一种充满前景的膜分离技术，具有出水水质高、运行压力低和运行温度低等优点在海水淡化方面显示出巨大的潜力。然而，由于相对较低的通量和长时间运行后膜性能的逐渐下降，截至当前，膜蒸馏并未实现商业化。所以，作为膜蒸馏过程的核心组件，开发一种高通量、高截留率和长使用寿命的膜蒸馏材料至关重要。当前，膜蒸馏过程中所采用的膜材料通常是由商业微滤膜制成的，如聚丙烯、聚偏氟乙烯和聚四氟乙烯中空纤维膜或平板膜等，这些膜材料不是专门为膜蒸馏设计的，在膜蒸馏过程中容易出现膜孔润湿和通量低的问题。理想的膜蒸馏膜应该具有疏水性强、孔隙率高、孔径分布范围窄和厚度小等特点。因此，迫切需要开发出适用于膜蒸馏过程的膜结构设计合理的超疏水膜，获得更好的膜蒸馏性能。静电纺...
【技术保护点】
1.一种膜蒸馏用多级结构亲疏水双层膜的制备方法，其特征在于，包括：(1)纺丝液的配置：将一定量的聚偏氟乙烯粉末和氟改性丙烯酸酯共聚物加入到N，N‑二甲基甲酰胺和丙酮的混合溶剂中，室温下搅拌使聚偏氟乙烯粉末和氟改性丙烯酸酯共聚物完全溶解，配置成质量分数为10～18％的聚偏氟乙烯溶液，所述的N，N‑二甲基甲酰胺和丙酮的体积比为1∶1～3∶1；所述的氟改性丙烯酸酯共聚物占聚偏氟乙烯溶液的质量百分比为1～5％；(2)膜蒸馏用亲疏水双层膜的制备：以聚偏氟乙烯/四丁基氯化铵体系制备的超亲水树枝状纳米纤维膜作为基布，采用静电纺丝技术对上述溶液进行静电纺丝，在亲水聚偏氟乙烯树枝状纳米纤维膜...
【技术特征摘要】
1.一种膜蒸馏用多级结构亲疏水双层膜的制备方法，其特征在于，包括：(1)纺丝液的配置：将一定量的聚偏氟乙烯粉末和氟改性丙烯酸酯共聚物加入到N，N-二甲基甲酰胺和丙酮的混合溶剂中，室温下搅拌使聚偏氟乙烯粉末和氟改性丙烯酸酯共聚物完全溶解，配置成质量分数为10～18％的聚偏氟乙烯溶液，所述的N，N-二甲基甲酰胺和丙酮的体积比...
【专利技术属性】
技术研发人员：厉宗洁，康卫民，刘雍，程博闻，赵义侠，李晓捷，庄旭品，鞠敬鸽，李磊，王利媛，邓南平，
申请(专利权)人：天津工业大学，
类型：发明
国别省市：天津,12