The invention relates to the technical field of supercapacitors. Specifically refers to the preparation method of nickel-cobalt alloy nanosheet arrays coated with sulfur, cobalt and nickel. The invention adopts carbon cloth as the base to grow Co-based metal-organic skeleton compounds as precursors, generates hollow nickel-cobalt bimetallic layered hydroxide nanosheet arrays by hydrothermal method, converts nickel-cobalt bimetallic layered hydroxides into nickel-cobalt alloy arrays by calcination method, and finally forms nickel coated with sulfur-cobalt nickel in situ on carbon cloth by hydrothermal sulfidation. Cobalt alloy nanosheet arrays.
【技术实现步骤摘要】
硫钴镍包覆的镍钴合金纳米片阵列的制备方法
本专利技术涉及超级电容器
，特指一种以Ni(NO3)2·6H2O、Co(NO3)2·6H2O、C4H6N2、CH3CSNH2和碳布为原料来制备的硫钴镍包覆的镍钴合金(NiCo-Alloy@NiCo-Sulfide)纳米片阵列材料，其制备工艺简单，成本低廉。技术背景能源与环境一直以来是人类社会发展所面临的两大问题。随着石化能源的不断开采与消耗，环境问题也日益突出，严重制约了人类社会的健康发展。因此，探索和研发新型、高效、清洁的能量储存与转换装置已成为人类社会可持续发展的战略性选择。超级电容器以其高的能量密度、功率密度和优秀的循环稳定性等特点受到了广泛的关注和应用。过渡金属硫化物基于自身优秀的理化性能，可形成多种纳米功能材料，尤其是作为电极材料被广泛的应用于超级电容器领域。NiCo-Sulfide作为一种双金属硫化物，因其协同的氧化还原反应和良好的导电性，相比于对应的氧化物和单金属硫化物具备更高的理论容量和更好的循环稳定性。迄今为止，NiCo-Sulfide双金属硫化已经被合成了不同形貌的纳米功能材料，例如纳米球、纳...
【技术保护点】
1.硫钴镍包覆的镍钴合金纳米片阵列的制备方法，其特征在于，采用碳布为基底，来生长Co基的金属有机骨架化合物作为前驱体，通过水热方法生成空心的镍钴双金属层状氢氧化物纳米片阵列，再通过煅烧的方法将镍钴双金属层状氢氧化物转化为镍钴合金阵列，最后进行水热硫化形成了碳布上原位生长的硫钴镍包覆的镍钴合金纳米片阵列。
【技术特征摘要】
1.硫钴镍包覆的镍钴合金纳米片阵列的制备方法，其特征在于，采用碳布为基底，来生长Co基的金属有机骨架化合物作为前驱体，通过水热方法生成空心的镍钴双金属层状氢氧化物纳米片阵列，再通过煅烧的方法将镍钴双金属层状氢氧化物转化为镍钴合金阵列，最后进行水热硫化形成了碳布上原位生长的硫钴镍包覆的镍钴合金纳米片阵列。2.如权利要求1所述的硫钴镍包覆的镍钴合金纳米片阵列的制备方法，其特征在于，具体步骤如下：(1)将碳布依次在丙酮、乙醇和水中分别超声后放入含有Co(NO3)2·6H2O和C4H6N2的混合水溶液中，室温静置反应，然后用水和乙醇交替清洗碳布后得到碳布上生长的Co基金属有机骨架化合物(CC@Co-MOF)前驱体；(2)将碳布上生长的CC@Co-MOF前驱体放入Ni(NO3)2·6H2O的乙醇溶液中，反应后得到碳布上生长的镍钴双金属层状氢氧化物纳米片阵列；(3)将所制备的碳布上生长的镍钴双金属层状氢氧化物纳米片阵列放入管式炉中，在氢氩混合气氛中煅烧，得到碳布上生长的镍钴合金纳米片阵列；(4)将所制备的碳布上生长的镍钴合金纳米片阵列放入CH3CSNH2的水溶液中，反应后用水清洗，得到碳布上生长的由核壳结构的硫钴镍包覆的镍钴合金纳米颗粒构成的纳米片阵列。3.如权利要求2...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。