The invention relates to a modified fiber foam concrete, and its components and weight parts are cement: Fly Ash: river sand: water: fiber: early strength powder: foaming agent: stable foam powder is 1000:333.3:333.3:833.3:6:5:11.7:2. The invention also relates to the dispersion method of the fiber and the preparation method of the fiber foam concrete. The modified fiber foamed concrete prepared by the invention has the advantages of light weight, high strength, high heat preservation and so on. It has the characteristics of wide application range, simple construction, energy saving, material saving, utilization of industrial waste, green environmental protection and so on.
【技术实现步骤摘要】
一种分散纤维泡沫混凝土及其制备方法
本专利技术涉及建筑材料
，尤其涉及一种分散纤维的方法以及一种轻质高强高保温改性纤维泡沫混凝土的制备方法。
技术介绍
随着建筑物向高层和超高层发展,减轻墙体自重成为众多设计师和开发商追逐的目标,同时也是建筑节能环保的要求,使轻质混凝土成为发展和研究的重点，其中泡沫混凝土近年来受到众多的关注和研究。泡沫混凝土是一种含有大量封闭气孔的新型轻质高强保温建筑材料，也是一种利废、环保、节能、低廉且具有不燃性的新型建筑节能材料。但因无粗骨料及多孔的结构特性，导致其存在强度偏低、易开裂等问题,限制了它的广泛应用。加入纤维可有效地解决上述问题。然而，普通纤维表面光滑，分子链上不含极性基团，具有极高的纵横比，掺入泡沫混凝土时极易团聚及与基体界面结合性能差。同时，由于密度较水泥材料小，搅拌过程中普遍存在分层离析现象。这些问题严重削弱了其作用效果。因此对其进行表面改性至关重要。据查阅相关资料，现有的改性纤维的方法主要有：１）利用某种表面活性剂对纤维改性，使其表面具有亲水的活性基团；２）利用超声波先对纤维进行分散。然而，这两种方法都存在显而易见的缺...
【技术保护点】
1.一种分散纤维泡沫混凝土，其特征在于，其组分及其重量份为水泥：粉煤灰：河沙：水：纤维：早强粉：发泡剂：稳泡粉为1000:333.3:333.3:833.3:6:5:11.7:2。
【技术特征摘要】
1.一种分散纤维泡沫混凝土，其特征在于，其组分及其重量份为水泥：粉煤灰：河沙：水：纤维：早强粉：发泡剂：稳泡粉为1000:333.3:333.3:833.3:6:5:11.7:2。2.根据权利要求1所述的分散纤维泡沫混凝土，其特征在于：所述水泥为硅酸盐类水泥、普通硅酸盐水泥或复合硅酸盐类水泥。3.根据权利要求1所述的分散纤维泡沫混凝土，其特征在于：所述粉煤灰为Ⅰ级粉煤灰。4.根据权利要求1所述的分散纤维泡沫混凝土，其特征在于：所述河沙为粒径小于≤0.3毫米。5.根据权利要求1所述的分散纤维泡沫混凝土，其特征在于：所述纤维为水溶性纤维，纤维长度≥9毫米，直径≤50微米。6.根据权利要求1所述的分散纤维泡沫混凝土，其特征在于：所述早强剂为甲酸钙白色粉末，分子式为C2H2CaO4。7.根据权利要求1所述的分散纤维泡沫混凝土，其特征在于：所述的发泡剂为聚合物发泡剂，稀释倍数为30倍，发泡倍数为34倍。8.根据权利要求1所述的分散纤维泡沫混凝土，其特征在于：所述稳泡剂为聚丙烯酰胺。9.一种分散纤维泡沫混凝土的制备方法，其特征是，包括如下步骤：（一）原材料及生产前准备：（1）将水按大于所述重量份称重后，放置室外...
【专利技术属性】
技术研发人员：陈艳，刘汉清，梅杏冰，刘子杰，
申请(专利权)人：汕头职业技术学院，
类型：发明
国别省市：广东,44