The invention relates to a foamed ceramic partition board and a preparation method thereof. The raw materials of the foamed ceramic partition board belong to the technical field of partition board. The raw materials of the foamed ceramic partition board include 50-85 parts of polished edge slag, 6-30 parts of flux and 2-10 parts of foaming agent by weight. The preparation method of the foamed ceramic partition board is to process the raw materials of the foamed ceramic partition board to make bricks. The foamed ceramic partition board made of the closed pore structure can greatly reduce the weight of the board and the water absorption of the board. The foamed ceramic partition board has the characteristics of no water content and low water absorption.
【技术实现步骤摘要】
发泡陶瓷隔墙板及其制备方法
本专利技术属于隔墙板
，具体而言，涉及一种发泡陶瓷隔墙板及其制备方法。
技术介绍
目前的轻质隔墙条板主要是空心混凝土条板、聚苯颗粒水泥复合板两种，以混凝土作为其主要原料，通过挤出机成形，以空心或混合填冲聚苯颗粒的方法作轻量化处理，再采用蒸气养护设备加速混凝土硬化，提高预制构件模具(台座)的周转频率、生产周期和综合经济效益。产品适用于建筑非承重内隔墙使用。具有标准化、定制化的产品特点。克服了传统灰沙砖、加气砌块施工周期长，施工墙面不平整的缺点。但是该类轻质隔墙条板重量重，吸水率偏大，收缩率大，容易产生裂纹等缺点，导致其使用寿命受到影响，该类轻质隔墙条板内墙应用中做贴墙纸等装饰容易脱落，影响墙面外观。
技术实现思路
本专利技术旨在至少解决现有技术中存在的重量重、吸水率偏大的问题。为此，本专利技术提出一种发泡陶瓷隔墙板。根据本专利技术第一方面实施例的发泡陶瓷隔墙板，其原料按重量份数计包括：陶瓷抛光磨边渣50－85份、助熔剂6－30份、发泡剂2－10份。上述技术方案中，陶瓷抛光磨边渣包括陶瓷砖生产过程中抛光磨边渣磨削所产生的废料。发泡陶瓷隔墙...
【技术保护点】
1.一种发泡陶瓷隔墙板，其特征在于，其原料按重量份数计包括：陶瓷抛光磨边渣50－85份、助熔剂6－30份以及发泡剂2－10份。
【技术特征摘要】
1.一种发泡陶瓷隔墙板，其特征在于，其原料按重量份数计包括：陶瓷抛光磨边渣50－85份、助熔剂6－30份以及发泡剂2－10份。2.根据权利要求1所述的发泡陶瓷隔墙板，其特征在于，所述助熔剂包括长石6－20份和滑石0－10份。3.根据权利要求2所述的发泡陶瓷隔墙板，其特征在于，所述长石包括钠长石、钾长石中的一种或者两种，所述滑石包括生滑石、熟滑石以及白滑石中的一种或者多种；可选地，所述长石为钾长石，所述滑石为白滑石。4.根据权利要求1－3任一项所述的发泡陶瓷隔墙板，其特征在于，发泡剂包括碳化硅、硅化钠以及炭黑中的一种或者多种；可选地，所述发泡剂为碳化硅。5.根据权利要求1－3任一项所述的发泡陶瓷隔墙板，其特征在于，其原料按重量份数计还包括稳定剂1.5－3.5份；可选地，所述稳定剂包括高岭土。6.根据权利要求1－3任一项所述的发泡陶瓷隔墙板，其特征在于，其原料按重...
【专利技术属性】
技术研发人员：潘顺源，黄永威，韦鸿会，冯正浩，
申请(专利权)人：广东华陶建材有限公司，
类型：发明
国别省市：广东,44